Structural elucidation and magnetic behavior evaluation of Cu-Cr doped BaCo-X hexagonal ferrites

Ba2-xCuxCo2CryFe28-yO46 (x = 0.0, 0.1, 0.2, 0.3, 0.4, y = 0.0, 0.2, 0.4, 0.6, 0.8) X-type hexagonal ferrites were synthesized via micro-emulsion route. The techniques which were applied to characterize the prepared samples are as follows: X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), Dielectric measurements and vibrating sample magnetometer (VSM). The structural parameters i.e. lattice constant (a, c), cell volume (V), X-ray density, bulk density and crystallite size of all the prepared samples were obtained using XRD analysis. The lattice parameters 'a' and 'c' increase from 5.875 angstrom to 5.934 angstrom and 83.367 angstrom to 83.990 angstrom respectively. The crystallite size of investigated samples lies in the range of 2832 nm. The magnetic properties of all samples have been calculated by vibrating sample magnetometer (VSM) analysis. The increase in coercivity (Hc) was observed with the increase of doping contents. It was observed that the coercivity (Hc) of all prepared samples is inversely related to the crystalline size which reflects that all materials are super-paramagnetic. The dielectric parameters i.e. dielectric constant, dielectric loss, tangent loss etc were obtained in the frequency range of 1 MHz-3 GHz and followed the Maxwell-Wagner's model. The significant variation the dielectric parameters are observed with increasing frequency. The maximum Q value is obtained at similar to 2 GHz due to which these materials are used for high frequency multilayer chip inductors. (C) 2017 Elsevier B.V. All rights reserved.