Formation of graphitic carbon nitride and boron carbon nitride film on sapphire substrate

As a novel production method of boron carbon nitride (BCN) films, in this paper, we present the incorporation of B into graphitic carbon nitride (g-C3N4). First, we investigated the formation of g-C3N4 films via chemical vapor deposition (CVD) using melamine powder as the precursor. The formation of g-C3N4 films on a c-plane sapphire substrate was confirmed by X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), and Raman spectroscopy measurements. The deposition temperature of g-C3N4 films was found to be suitable between 550 and 600 degrees C since the degradation and desorption of hexagonal C-N bonds should be suppressed. As for BCN films, we prepared BCN films via two-zone extended CVD using ammonia borane as the B precursor. Several XPS signals from B, C, and N core levels were detected from B-incorporated g-C3N4 films. While the N composition was almost constant, the marked tendencies for increasing B composition and decreasing C composition were achieved with the increase in the B incorporation, indicating the incorporation of B atoms by the substitution for C atoms. Optical absorptions were shifted to the high-energy side by B incorporation, which indicates the successful formation of BCN films using melamine and ammonia borane powders as precursors. (C) 2018 The Japan Society of Applied Physics