Effect of synthesis and activation methods on the catalytic properties of silica nanospring (NS)-supported iron catalyst for Fischer-Tropsch synthesis

A nanostructured iron (Fe) catalyst for Fischer-Tropsch synthesis (FTS) was prepared and evaluated using a silica nanospring (NS) support. FTS offers an approach of producing biofuels from synthesis gas (syngas) produced via biomass gasification. The Fe/NS catalysts were prepared using three different methods: (i) incipient wetness impregnation, (ii) precipitation and (iii) modified sol-gel, in order to obtain different sizes of deposited Fe nanoparticles on the NS support and investigate the influence of particle size on FTS. The Fe decorated catalysts were calcined and then activated with either H-2, CO or H-2 + CO mixture. The prepared Fe/NS catalysts were characterized before the FT reaction by BET surface area, X-ray diffraction (XRD), transmission electron microscopy (TEM), temperature programmed reduction (TPR), X-ray photoelectron spectroscopy (XPS) and thermogravimetric analysis (TGA) in order to fmd correlations between physico-chemical properties of catalysts and catalytic performance. The decoration of Fe nanoparticles of different sizes onto NS using the various methods ranged from 1.7 to 10 nm. The FTS performance was also evaluated in a quartz fixed-bed microreactor (H-2/CO of 2:1, 270 degrees C) and the products trapped and analyzed by GC-TCD and GC MS to determine CO conversion and reaction selectivity. These results show that the highest CO conversion (76.6%) and a wide distribution of light hydrocarbon (C-6 to C-14) were obtained for Fe/NS catalyst prepared by impregnation and activated with CO after 12 h of the FT reaction.