期刊
CERAMICS INTERNATIONAL
卷 44, 期 13, 页码 15411-15417出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2018.05.193
关键词
Powders: solid state reaction; Optical properties; Niobates; Sensors
资金
- National Natural Science Foundation of China [51572195]
Pr3+/Gd3+ co-doped LiNbO3 phosphors were prepared by a traditional solid-state reaction method and their structure, photoluminescence, mechanoluminescence and thermoluminescence were investigated. The results showed that the LiNbO3 phase with a rhombohedral structure and an R3c space group was successfully prepared. Mechanoluminescence intensity in nonstoichiometric LiNbO3 :Pr3+ was largely increased by introducing Gd3+ ions. The optimal co-doped concentration of Gd3+ was 1 mol% and the enhanced ML intensity of LiNbO3 :0.01Pr(3+), 0.01Gd 3 +/- was about 177% times compared with that of LiNbO3:0.01Pr(3+). The effect of Gd 3+ co-dopants on trap levels were explored through thermoluminescence curves. The enhancement of mechanoluminescence intensity was suggested to be ascribed to the regulated trap quantities caused by co-doped Gd3+ ions. Appropriate co-dopants are proved to be effective sensitizers for mechanoluminescence materials.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据