期刊
CEMENT AND CONCRETE RESEARCH
卷 105, 期 -, 页码 1-17出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.cemconres.2017.11.007
关键词
Thermal analysis (B); X-ray diffraction (B); Ca(OH)(2) (D); Blended cement (D); Dedolomitization reaction
资金
- Norwegian Research Council
- Heidelberg Technology Center [241637]
This study focuses on the reaction of dolomite powder in combination with metakaolin in Portland composite cement pastes. We studied paste samples cured at 20 degrees C, 38 degrees C, and 60 degrees C for up to 1 year. In these systems, the only magnesium-containing hydration phase of dolomite observed was hydrotalcite. Dolomite reacted notably already after 90 days when cured at 60 degrees C, whereas at lower curing temperatures the reaction was limited. The increased availability of aluminium due to the addition of metakaolin did not contribute to the formation of hydrotalcite. The refined pore space due to the metakaolin addition did not inhibit the hydrotalcite formation. However, the almost total absence of portlandite due to the pozzolanic reaction of the metakaolin inhibited the dolomite reaction, even in pastes with high porosity. Portlandite seems to be the driving force for the reaction as its absence is inhibiting the reaction to take place.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据