Microstructure and opto-electronic properties of Sn-rich Au-Sn diffusive solders

Microstructural and opto-electronic properties of Au/Sn and Sn\Au bilayers, obtained by sequential evaporating of metals on the Si substrate, were investigated by means of atomic force microscopy, X-ray diffraction and spectroscopic ellipsometry. Thicknesses of individual films were established to obtain the atomic ratio of Au:Sn atoms 1: 1, 1: 2 and 1: 4, which were favor the formation of AuSn, AuSn2 and AuSn4, respectively. However, the produced intermatallic compounds were detected as AuSn and AuSn2. Additionally, the unbounded Sn was found. The sequence of deposition of Au and Sn films as well as their thickness strongly affect on the composition, microstructure, optical and electrical properties of the produced layers. The Au/Sn (Sn on the top) layers were more smooth than Sn\Au (Au on the top) films. Generally, the Au/Sn layers exhibit a better electrical and optical properties than Sn\Au films. The optical parameters: plasma energy, free-carrier damping, mean relaxation time of conduction electrons and optical resistivity were determined from the effective complex dielectric function of the formed Au, Sn and Au-Sn films. The optical resistivity values are in the range from 17.8 mu Omega cm to 85.1 mu Omega cm and from 29.6 mu Omega cm to 113.3 mu Omega cm for Au/Sn and Sn\Au layers, respectively. (C) 2018 Elsevier B.V. All rights reserved.