期刊
METALS
卷 7, 期 5, 页码 -出版社
MDPI AG
DOI: 10.3390/met7050181
关键词
high-chromium vanadium-titanium magnetite; calcium oxide; crushing strength; reduction and smelting
资金
- National Project Support Program in China [2015BAB19B02]
- 973 Program [2013CB632603]
The effect of calcium oxide on the crushing strength, reduction, and smelting performance of high-chromium vanadium-titanium magnetite pellets (HCVTMP) was studied in this work. The main characterization methods of an electronic universal testing machine (EUTM), X-ray fluorescent (XRF), inductively-coupled plasma-atomic emission spectroscopy (ICP-AES), X-ray diffraction (XRD), and scanning electron microscope-energy disperse spectroscopy (SEM-EDS) were employed. The crushing strength was affected by the mineral phases generated during oxidative baking and the subsequently-formed pellet microstructures owing to CaO addition. The reduction and smelting properties of HCVTMP with different CaO additives were measured and characterized with different softening-melting-dripping indices. Although HCVTMP showed the highest crushing strength with CaO addition of ca. 2 wt %, more CaO addition may be needed to achieve high permeability of the furnace burdens and a good separation condition of the slag and melted iron. In the formation process of the slag and melted iron, it can be determined that CaO could have a relationship with the transformation behavior of Cr, V, and Ti to some extent, with respect to the predominant chemical composition analysis of ICP-AES and XRF. With the microscopic examination, the restraining formation of Ti(C, N) and the promoting formation of CaTiO3 are in accordance with the improved melting-dripping indices, including the decrease of the maximum external static load and gas permeability, and the increase of the melting-dripping zone and dripping difficulty.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据