Superplasticity; Al-Mg alloy; Sc; Dynamic recrystallization
类别
资金
- National Key Basic Research Program of China (973 Program) [2012CB619503]
The superplastic behavior of Al-Mg-Sc-Zr samples with standard gauge size (18 mm by 6 mm) were prepared using simple rolling and were tested in the temperature range from 450 degrees C to 525 degrees C at strain rates ranging from 1.67x10(3)s(-1) to 1 x10(-1) s(-1). With proper deformation parameters, the Al-Mg-Sc-Zr alloy has an elongation to failure much higher than 300% and the maximum elongation is 740%. The Microstructure and dislocation substructure investigation using optical microscopy (OM) and transmission electron microscopy (TEM) revealed a dynamic recrystallization in it. The grain size and activation energy on the deformation mechanisms of superplastic is discussed. Results also show that these nano-scale A1(3)(Sc-1x,Zr-x(x)) particles play an important role in the superplastic process. Al6FeMn particles were found to induce the formation and growth of cavities, which can lead to the fracture of specimens.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据