Synthesis and color performance of CaCoSi2O6 pyroxene, a new ceramic colorant

The pyroxene structure was successfully used as a crystalline host for a new Co-based pink pigment. Different compositions of Ca1-xCo1+xSi2O6 (0 <= x <= 1) powders were prepared by using the solid state method with different temperatures and times of annealing. The characterization of the fired samples was performed by X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), colorimetry and technological tests simulating the ceramic applications. A monophasic pink clinopyroxene was obtained for compositions close to the CaCoSi2O6 end-member. For increasing cobalt content, an assemblage of Co-olivine, Co-akermanite and Ca,Co-pyroxene was found. Samples containing Co-akermanite have a deep blue color stemming from Co2+ in tetrahedral coordination, while those with Co-olivine are violet due to Co2+ in octahedral coordination. The best conditions for the synthesis of a CaCoSi2O6 single phase were then investigated, finding that a proper annealing cycle at 1150 degrees C prevents the formation of metastable Co-akermanite. The CaCoSi2O6 Pyroxene was tested as a ceramic pigment into glazes and glassy coatings. In most cases, it behaves like a dye, completely dissolving in the melted glaze, analogously to Co-olivine. (C) 2015 Elsevier Ltd. All rights reserved.