期刊
JOURNAL OF SOLID STATE CHEMISTRY
卷 253, 期 -, 页码 389-397出版社
ACADEMIC PRESS INC ELSEVIER SCIENCE
DOI: 10.1016/j.jssc.2017.06.021
关键词
Na2Mn1.5Fe1.5(PO4)(3); Alluaudite structure type; Hydrothermal synthesis; Crystal structure refinement; Mossbauer spectroscopy; Energy storage
资金
- Walloon Region [BATWAL - 1318146, 1510399]
- University of Liege
- FRS-FNRS
- U.S. Department of Energy [DE-AC05-000R22725]
The sodium-manganese-iron phosphate Na2Mn1.5Fe1.5(PO4)(3) (NMFP) with alluaudite structure was obtained by a one-step hydrothermal synthesis route. The physical properties and structure of this material were obtained through XRD and Mossbauer analyses. X-ray diffraction Rietveld refinements confirm a cationic distribution of Na+ and presence of vacancies in A(2)', Na+ and small amounts of Mn2+ in A(1), Mn2+ in M(1), 0.5 Mn2+ and Fe cations (Mn2+,Fe2+ and Fe3+) in M(2), leading to the structural formula Na2Mn(Mn0.3Fe1.$) (PO4)3. The particles morphology was investigated by SEM. Several reactions with different hydrothermal reaction times were attempted to design a suitable synthesis protocol of NMFP compound. The time of reaction was varied from 6 to 48 h at 220 degrees C. The pure phase of NMFP particles was firstly obtained when the hydrothermal reaction of NMFP precursors mixture was maintained at 220 degrees C for 6 h. When the reaction time was increased from 6 to 12, 24 and 48 h, the dandelion structure was destroyed in favor of NMFP micro-rods. The combination of NMFP (NMFP-6H, NMFP-12H, NMFP-24H and NMFP-48H) structure refinement and Mossbauer characterizations shows that the increase of the reaction time leads to the progressive increment of Fe(III) and the decrease of the crystal size. The electrochemical tests indicated that NMFP is a 3 V sodium intercalating cathode. The comparison of the discharge capacity evolution of studied NMFP electrode materials at C/5 current density shows different capacities of 48, 40, 34 and 34 mA h g(-1) for NMFP-6H, NMFP-12H, NMFP-24H and NMFP-48H respectively. Interestingly, all samples show excellent capacity retention of about 99% during 50 cycles.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据