Fluorinated polyimide thin films; porous; silica microsphere; template; ultralow dielectric constant
资金
- Nature Science Foundation of China (NSFC) [51403219]
In this paper, silica microspheres were used as template to prepare porous fluorinated polyimide (FPI) thin films from polyamic acid (PAA, precursor of FPI) and silica colloid solution. The strong hydrogen-bonding interaction between silica microspheres and PAA chains have improved the dispersion of silica microspheres in N,N-Dimethylformamide (DMF) solution, resulting in the high weight content of silica template in PAA/silica colloid solution, and thus giving rise to the formation of porous FPI films with maximum porosity of 35%. The interior microstructures of the resultant porous FPI thin films were investigated. It is found that the porous FPI thin films have interconnected ink-bottle-type porous structure, and the pore size, porosity could be precisely controlled by the diameter and weight content of silica microspheres, respectively. Although both the tensile strength and young modules declined with the increasing porosity, the high level void of the porous FPI films endowed the FPI ultralow dielectric constant of 1.84 when the porosity increased to 35%. Furthermore, the mechanical and dielectric properties of the porous FPI films were closely related to the microstructures and porosity, indicating the desired properties could be controlled to meet the application in the microelectronics.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据