A brand new HfB2-SiC-MoSi2 coating was fabricated to protect carbon/carbon (C/C) composites with inner SiC coating from oxidation, which was prepared by in-situ synthesis. In this paper, the C/C substrate with the protection of the HfB2-SiC-MoSi2/SiC coating could resist oxidation in 1773 K air for 408 h. The double coating also presented expected oxidation protection performance at dynamic oxidation environment. In the test process, the surface coating was oxidized to form a self-sealing silicate glass layer containing HfO2 and HfSiO4, which could hinder crack propagation in coating. (C) 2017 Published by Elsevier B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据