JOURNAL OF ALLOYS AND COMPOUNDS
卷 713, 期 -, 页码 255-265出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2017.04.172
关键词
Work function; Wear behavior; Friction coefficient; Wear rate
In this paper, work function and dry sliding wear behavior of the hardfacing alloys with different content of nano rare earth oxides (REOs) were studied. The microstructural changes of the hardfacing alloys with and without nano REOs were observed. The integral work function of hardfacing alloys was measured by Scanning Kelvin Probe. The individual work function of the constituent phases was indirectly measured and compared by Atomic Force Microscope. Pin-on-disc wear testing machine was used to conduct dry sliding wear tests. The results showed that nano REOs changed the volume fractions of primary carbide, eutectic carbide and the matrix. Nano REOs increased the integral work function of hardfacing alloys by increasing the volume fraction of primary carbide with high work function. The work functions of primary carbide and eutectic carbide were similar, which were higher than that of the matrix. Nano REOs improved the wear resistance of hardfacing alloys. The variation trends of friction coefficient and integral work function with the content of nano REOs were reversed. The variation trends of wear rate and integral work function with the content of nano REOs were also reversed. The hardfacing alloy having higher integral work function had better wear resistance. (C) 2017 Published by Elsevier B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据