THEORETICAL AND APPLIED FRACTURE MECHANICS
卷 85, 期 -, 页码 45-55出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.tafmec.2016.08.015
关键词
Crack tip opening displacement (CTOD); Crack closure; Fatigue threshold; Aluminum alloy
The crack tip opening displacement, CTOD, is a classical parameter of fracture mechanics. The applicability of this parameter in the context of crack closure and fatigue crack growth is studied. An elastic-plastic finite-element model was developed to quantify the CTOD in a M(T) specimen for two aluminum alloys (AA6016-T4 and the AA6082-T6). An elastic regime was found for relatively low loads, and its upper bound was used to quantify the fatigue threshold. The plastic CTOD was found to be a measure of crack tip plastic deformation and an intimate relation was found with other non-linear crack tip parameters. Analysis without contact of crack flanks showed the validity of crack closure concept. No influence of stress state on plastic CTOD was found in the absence of crack closure, which indicates that the effect of this parameter is linked to crack closure effects. Finally, a relation was found between da/dN and plastic CTOD for the AA6082-T6 aluminum alloy, independent of stress ratio, showing that the plastic CTOD is an interesting alternative to Delta K in the analysis of fatigue crack propagation. (C) 2016 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据