Aluminum alloys; Mechanical properties; Microstructure; Powder consolidation; Quasicrystal
类别
资金
- Pratt Whitney
- University of Connecticut Research Foundation
Nanocomposite powder particles of aluminum with dispersed icosahedral quasicrystals were produced by gas atomization from an Al-Cr-Mn-Co-Zr alloy. Bulk dispersion -strengthened material was obtained from the powder by blind-die compaction and forging. The material exhibited an attractive combination of room temperature mechanical properties with a dynamic elastic modulus of 90.5 GPa, a tensile yield strength of 690 MPa with 6% elongation to failure, and a high cycle fatigue life of 109 cycles at 207 MPa applied stress. The material also exhibited significant potential for elevated temperature applications with a modulus of 75 GPa and yield strength of 400 MPa at 300 degrees C. (C) 2016 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据