CHINESE JOURNAL OF POLYMER SCIENCE
卷 33, 期 7, 页码 1028-1037出版社
SPRINGER
DOI: 10.1007/s10118-015-1643-x
关键词
Annealing; Microporous membrane; Polypropylene; Crystalline orientation; Deformation behavior
资金
- National Natural Science Foundation of China [51273132]
- Chinese Scholarship Council (CSC)
In this work, the effects of annealing conditions on the microstructure of polypropylene (PP) precursor films and further on the porous structure and permeability of stretched membranes were investigated. Combinations of WAXD, FTIR, DSC and DMA results clearly showed the crystalline orientation and crystallinity of the precursor film increased with annealing temperature, while the molecular chain entanglements in the amorphous phase decreased. Changes in the deformation behavior suggested more lamellar separation occurred for the films annealed at higher temperatures. Surface morphologies of the membranes examined by SEM revealed more pore number and uniform porous structure as the annealing temperature increased. In accordance with the SEM results, the permeability of the membranes increased with annealing temperature. On the other hand, it was found that 10 min was almost enough for the annealing process to obtain the microporous membranes with an optimal permeability.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据