Polyaniline was synthesized chemically in an acidic medium in the presence of Ammonium Peroxydisulphate (APS) as an oxidizing agent. PANI(Polyaniline) nanocomposites were prepared in the presence of various amount of carbon nanotube and zinc oxide (from 1 to 5 wt%) by solution casting method. The free-standing film of polyaniline and its nanocomposites were obtained by vaporization of solvent content. The composition, morphology and structure of the polymer and the nanocomposites were characterized by Fourier transform infrared spectroscopy FT-IR spectra, scanning electron microscopy (SEM) image and XRD pattern. In addition, thermal stability was studied by TGA analysis, electrical conductivity was measured by four-point probe technique and mechanical properties were studied by tensile strength test. The characteristic FTIR peaks of PANI were found to shift to lower wave number in nanocomposites due to the formation of H-bonding. XRD results revealed that the crystallinity of PANI was more noticeable after addition of nano-ZnO, while the intensity of the peaks increased by the addition of ZnO nanoparticles. Furthermore, TGA results showed that the decomposition of the nanocomposite was less than that of pure polyaniline which confirms the successful fabrication of products. Young's modulus and strength at break point were increased in the case of the nanocomposite, in addition, the electrical conductivity of the PANI/ZnO nanocomposite film was found to be smaller than that of the PANI film while CNTs increase the conductivity of polyaniline.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据