Impact of Rare Earth Ions (Ce and Gd) on Structural and Magnetic Properties of Nanostructured Ni-Zn Ferrites

Present work focuses to investigate the impact of rare earth ions (Ce and Gd) on the structural and magnetic properties of nanocrystalline nickel-zinc ferrite. The nanoparticles of Ni0.5Zn0.5Fe2O4, Ni0.5Zn0.5Ce0.02Fe1.98O4, and Ni0.5Zn0.5Gd0.02Fe1.98O4 were synthesized by citric acid-assisted sol-gel method. The formation of cubic spinel structure without additional impurity peaks was confirmed by X-ray diffraction (XRD) pattern. The crystallite size of Ni0.5Zn0.5Fe2O4 (R = 0) and Ni0.5Zn0.5R0.02Fe1.98O4 (R = Ce and Gd) nanoparticles was observed less than similar to 35 nm at sintering temperatures of similar to 300 to similar to 500 degrees C. From magnetic measurements, the value of room temperature saturation magnetization of superparamagnetic Ni0.5Zn0.5Fe2O4 (R = 0) was found to be reduced with the doping of Ce and Gd ions from 44.19 +/- 0.02 to 39.33 +/- 0.03 emu/g and 35.18 +/- 0.02 emu/g, respectively, at 300 degrees C and from 60.69 +/- 0.04 to 54.11 +/- 0.03 emu/g and 55.72 +/- 0.04 emu/g, respectively, at 500 degrees C. The detailed study of superparamagnetic relaxation in pure and rare earth-doped samples was performed by the thermal magnetization measurements under zero field cool (ZFC) and field cool (FC) processes. Mossbauer spectra revealed the absence of the quadrupole splitting for Ni0.5Zn0.5Ce0.02Fe1.98O4 at tetrahedral (A-site) and octahedral (B-site) sites which indicated cubic symmetry in the crystal structure. Although, the presence of negative asymmetry was observed in Ni0.5Zn0.5Gd0.02Fe1.98O4-doped ferrite sample. Magnetic materials with superparamagnetic properties are desirable in various biomedical applications.

Automated summary

This study investigates the impact of rare earth ions (Ce and Gd) on the structural and magnetic properties of nanocrystalline nickel-zinc ferrite. The results show that the doping of rare earth ions reduces the saturation magnetization and affects the crystal structure of the material.