期刊
MICROPOROUS AND MESOPOROUS MATERIALS
卷 221, 期 -, 页码 212-219出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.micromeso.2015.09.047
关键词
Clays; Montmorillonite; Intercalation; Exfoliation; Iron oxide
类别
资金
- Polish National Science Centre [N N507 217640]
- European Regional Development Fund [POIG.02.01.00-12-023/08]
- DOCTUS scholarship
- European Social Fund
A synthesis of metal oxide modified clays based on the hydrogel template assisted route was proposed. This novel method was verified by an intercalation of poly(acrylic acid) (PAA) into the interlayer space of montmorillonite (MT) using the in situ polymerization technique. The obtained hydrogel/clay composite with a MT/PAA mass ratio close to 1.0 exhibited an expanded layered structure and an excellent adsorption capacity for transition metal cations. These features were exploited to the modification of MT-FAA material with various amounts of Fe3+ cations by deposition at controlled pH = 2.5. The introduced Fe species favored the hydrogel burning, therefore in a subsequent step the organic template could be easily removed by calcination under oxidizing conditions at temperature protecting the clay against deep dehydroxylation. A gradual delamination of MT with an increase in the Fe content was observed after thermal treatment. This effect resulted in opening of the MT structure, manifested by a relatively high surface area and a large porosity. XRD, TEM, UV Vis-DRS and XPS measurements exhibited that the formed alpha-Fe2O3 nanoparticles were highly dispersed on the exfoliated clay, which comprised a framework stabilizing the nanophase. (C) 2015 Elsevier Inc. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据