Compressive anisotropy effects and crack evolution mechanisms of 3D5d braided composites induced by thermo-oxidative ageing
出版年份 2023 全文链接
标题
Compressive anisotropy effects and crack evolution mechanisms of 3D5d braided composites induced by thermo-oxidative ageing
作者
关键词
-
出版物
COMPOSITES SCIENCE AND TECHNOLOGY
Volume 240, Issue -, Pages 110102
出版商
Elsevier BV
发表日期
2023-05-29
DOI
10.1016/j.compscitech.2023.110102
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- Micro-CT based parametric modeling and damage analysis of three-dimensional rotary-five-directional braided composites under tensile load
- (2023) Zhi-Jian Li et al. COMPOSITE STRUCTURES
- Thermal oxygen coupling effects on multiple-layer degradation behaviors and full-field crack evolutions of 3D5d braided composites
- (2023) Jing Long et al. COMPOSITES SCIENCE AND TECHNOLOGY
- Impact compression damages of 3D braided composites with/without axial yarns after thermo-oxidative ageing
- (2022) Jing Long et al. INTERNATIONAL JOURNAL OF DAMAGE MECHANICS
- Longitudinal compression fatigue properties of 3D five-directional braided composites at different temperatures
- (2022) Hong-mei Zuo et al. COMPOSITE STRUCTURES
- Strain rate effect on compressive damages of thermo-oxidative aged 3D braided composites
- (2022) Jing Long et al. ENGINEERING FRACTURE MECHANICS
- Multiscale modeling of the mechanical behavior of 3D braided CFRP composites under uniaxial tension
- (2022) Yutong Liu et al. COMPOSITE STRUCTURES
- In Situ Investigation of Failure in 3D Braided SiCf/SiC Composites under Flexural Loading
- (2021) Changqi Liu et al. COMPOSITE STRUCTURES
- Microstructure modeling multiple transverse impact damages of 3-D braided composite based on thermo-mechanical coupling approach
- (2021) Meiqi Hu et al. COMPOSITES PART B-ENGINEERING
- Near-fiber nanomechanical mapping and impact failure mechanism of 3D braided composites subjected to thermo-oxidative environment
- (2021) Yuanyuan Wu et al. COMPOSITES SCIENCE AND TECHNOLOGY
- Micro-CT based trans-scale damage analysis of 3D braided composites with pore defects
- (2021) Lei Ge et al. COMPOSITES SCIENCE AND TECHNOLOGY
- Evolution of fibre deflection leading to kink-band formation in unidirectional glass fibre/epoxy composite under axial compression
- (2021) Ying Wang et al. COMPOSITES SCIENCE AND TECHNOLOGY
- Digital image and volume correlation with X-ray micro-computed tomography for deformation and damage characterisation of woven fibre-reinforced composites
- (2021) John Holmes et al. COMPOSITE STRUCTURES
- Full-field progressive fatigue damage of 3D5D braided composites with yarn-reduction: visualization, classification, and quantification
- (2021) Xiaodong Liu et al. COMPOSITES SCIENCE AND TECHNOLOGY
- Damage initiation and propagation mechanisms of 3-D angle-interlock woven composites under thermo-oxidative aging
- (2020) Yanan Ke et al. COMPOSITE STRUCTURES
- Multi-scale ageing mechanisms of 3D four directional and five directional braided composites’ impact fracture behaviors under thermo-oxidative environment
- (2019) Baohui Shi et al. INTERNATIONAL JOURNAL OF MECHANICAL SCIENCES
- A coupled FE-FFT multiscale method for progressive damage analysis of 3D braided composite beam under bending load
- (2019) Guodong Fang et al. COMPOSITES SCIENCE AND TECHNOLOGY
- Improving the open-hole tension characteristics with variable-axial composite laminates: Optimization, progressive damage modeling and experimental observations
- (2019) José Humberto S. Almeida et al. COMPOSITES SCIENCE AND TECHNOLOGY
- Micro-XCT analysis of damage mechanisms in 3D circular braided composite tubes under transverse impact
- (2018) Haili Zhou et al. COMPOSITES SCIENCE AND TECHNOLOGY
- Experimental and numerical analyses of matrix shrinkage and compressive behavior of 3-D braided composite under thermo-oxidative ageing conditions
- (2018) Man Zhang et al. COMPOSITE STRUCTURES
- Effects of off-axis angle on shear progressive damage of 3D woven composites with X-ray micro-computed tomography
- (2018) Diantang Zhang et al. COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING
- A multiscale elasto-plastic damage model for the nonlinear behavior of 3D braided composites
- (2018) Chunwang He et al. COMPOSITES SCIENCE AND TECHNOLOGY
- Meso-structure ageing mechanism of 3-D braided composite's compressive behaviors under accelerated thermo-oxidative ageing environment
- (2017) Man Zhang et al. MECHANICS OF MATERIALS
- Assessment of thermo-oxidative induced chemical strain by inverse analysis of shrinkage profiles in unidirectional composites
- (2016) M. Gigliotti et al. COMPOSITE STRUCTURES
- Influence of fibre architecture on the tensile, compressive and flexural behaviour of 3D woven composites
- (2015) S. Dai et al. COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING
- Anisotropic oxidation due to aging in a triaxially braided composite and its influence on tensile failure
- (2015) Amine El Mourid et al. COMPOSITES PART B-ENGINEERING
- Experimental investigation on the compression properties and failure mechanism of 3D braided composites at room and liquid nitrogen temperature
- (2013) Dian-sen Li et al. COMPOSITES PART B-ENGINEERING
- The effect of thermo-oxidation on matrix cracking of cross-ply [0/90]S composite laminates
- (2012) Dinh-Quy Vu et al. COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING
- A comparison of multi-scale 3D X-ray tomographic inspection techniques for assessing carbon fibre composite impact damage
- (2012) D.J. Bull et al. COMPOSITES SCIENCE AND TECHNOLOGY
Discover Peeref hubs
Discuss science. Find collaborators. Network.
Join a conversationAsk a Question. Answer a Question.
Quickly pose questions to the entire community. Debate answers and get clarity on the most important issues facing researchers.
Get Started