期刊
MEASUREMENT
卷 94, 期 -, 页码 902-908出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.measurement.2016.09.030
关键词
CaCu3Ti4O12; Alumina substrate; RH sensor; Response time; Recovery time; Sensitivity; Ag electrode
资金
- Universiti Sains Malaysia (USM) fellowship [APEX 91002/JHEA/ATSG4001]
- fundamental research grant scheme (FRGS) [203/PBAHAN/607126]
A resistance type humidity sensor has been fabricated from an assembly of CaCu3Ti4O12 thick film, Ag interdigitated electrodes, and an Al2O3 ceramic substrate. The humidity sensing properties were measured using the direct current (DC) analysis method. The results show that the electrical properties of the CaCu3Ti4O12 thick film are dependent on humidity and applied voltage. At low humidity, the film exhibited low conductivity and behaved as an insulator. However, at high humidity, the conductivity of the film increased due to the enhancement of ion conduction. These outcomes indicate that the measured resistance is highly dependent on the applied bias voltage within the whole humidity range i.e. 20-90% relative humidity (RH) at ambient temperature. The response and recovery times as well as sensitivity were determined to be around 2.8 min, 25 min, and 98.2%, respectively. Therefore, it is concluded that CaCu3Ti4O12 thick film has good humidity sensing properties and has high potential in the application for fabrication of high-performance humidity sensors. (C) 2016 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据