Research on the Effect of Pearlite Lamellar Spacing on Rolling Contact Wear Behavior of U75V Rail Steel
出版年份 2023 全文链接
标题
Research on the Effect of Pearlite Lamellar Spacing on Rolling Contact Wear Behavior of U75V Rail Steel
作者
关键词
-
出版物
Metals
Volume 13, Issue 2, Pages 237
出版商
MDPI AG
发表日期
2023-01-27
DOI
10.3390/met13020237
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- Wear properties of two U71Mn K and U71Mn G rail steel welds during rolling contact fatigue
- (2019) Jinfang Peng et al. INTERNATIONAL JOURNAL OF MODERN PHYSICS B
- Fatigue behavior and microstructural characterization of a high strength steel for welded railway rails
- (2018) R. Baptista et al. INTERNATIONAL JOURNAL OF FATIGUE
- Failure analysis of recurrent cases of fatigue fracture in flash butt welded rails
- (2015) L.B. Godefroid et al. ENGINEERING FAILURE ANALYSIS
- Effects of retained austenite and hydrogen on the rolling contact fatigue behaviours of carbide-free bainitic steel
- (2013) Chunlei Zheng et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Wheel and rail wear—Understanding the effects of water and grease
- (2013) C. Hardwick et al. WEAR
- Extremely fine pearlite by continuous cooling transformation
- (2012) K.M. Wu et al. SCRIPTA MATERIALIA
- Adhesion modeling in the wheel–rail contact under dry and lubricated conditions using measured 3D surfaces
- (2012) Yi Zhu et al. TRIBOLOGY INTERNATIONAL
- A study of rolling contact fatigue crack growth in U75V and U71Mn rails
- (2011) W. Zhong et al. WEAR
- Progressive damage assessment in the near-surface layer of railway wheel–rail couple under cyclic contact
- (2010) G. Donzella et al. WEAR
- On-site investigation and analysis of flaking damage leading to rail break
- (2010) Hiroyuki Matsuda et al. WEAR
- RCF and wear in theory and practice—The influence of rail grade on wear and RCF
- (2010) R. Stock et al. WEAR
- Introduction to the damage tolerance behaviour of railway rails – a review
- (2009) U. Zerbst et al. ENGINEERING FRACTURE MECHANICS
- Competition between wear and rolling contact fatigue at the wheel—rail interface: some experimental evidence on rail steel
- (2009) G Donzella et al. PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART F-JOURNAL OF RAIL AND RAPID TRANSIT
- A numerical model of twin disc test arrangement for the evaluation of railway wheel wear prediction methods
- (2009) N. Tassini et al. WEAR
- Rolling–sliding laboratory tests of friction modifiers in dry and wet wheel–rail contacts
- (2009) O. Arias-Cuevas et al. WEAR
- The effects of top of rail friction modifier on wear and rolling contact fatigue: Full-scale rail–wheel test rig evaluation, analysis and modelling
- (2008) Donald T. Eadie et al. WEAR
- Modelling thermal effects in ratcheting-led wear and rolling contact fatigue
- (2008) I.M. Widiyarta et al. WEAR
- An investigation into the causes of squats—Correlation analysis and numerical modeling
- (2008) Zili Li et al. WEAR
- Twin disc assessment of wheel/rail adhesion
- (2008) E.A. Gallardo-Hernandez et al. WEAR
Find Funding. Review Successful Grants.
Explore over 25,000 new funding opportunities and over 6,000,000 successful grants.
ExploreCreate your own webinar
Interested in hosting your own webinar? Check the schedule and propose your idea to the Peeref Content Team.
Create Now