Nanostructured ionic conductors have recently attracted our attention due to the expectation that they may lead to new functionalities absent in microcrystalline conductors. In this study, nanostructured barium zirconate with perovskite crystal structure was prepared and its grain and grain boundary protonic conduction was investigated using ac impedance measurements as a function of temperature (RT similar to 400 degrees C) andwater partial pressure. The grain was highly conductive of protons, which is governed by the concentration of protonic defects at all temperatures. On the other hand, the grain boundary was not the preferred route for protonic conduction due to high resistance. However, enhanced protonic transport was observed at certain temperatures (< 100 degrees C). The protonic resistivity below that temperature decreased with decreasing temperature, showing positive activation energy in relation to temperature. The conduction route for the enhanced transport was the serial grain boundary. In addition, the route was compared with that of nanostructured zirconia with fluorite crystal-structure.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据