CERAMICS INTERNATIONAL
卷 48, 期 20, 页码 30462-30467出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2022.06.326
关键词
Silicon carbide; Ceramic; Fly ash; Sintering aid; Low temperature
资金
- Science and Technology Program in Education Department of Jilin Province [JJKH20220122KJ]
- Science and Technology Development Program of the Jilin Province [20200301030RQ]
By adding fly ash, high-quality silicon carbide foam ceramics were successfully fabricated at a low sintering temperature, which significantly reduced the fabrication cost and enhanced the commercial application.
Silicon carbide (SiC) foam ceramics (SFC) have been widely used in various industries owing to their excellent mechanical properties at elevated temperatures. However, fabricating a qualified product at a low sintering temperature is a challenge because of the strong covalent nature of the Si-C bond. In this study, we successfully fabricated a SFC at a low sintering temperature (1150 degrees C) by adding fly ash (FA) using the polyurethane replication method. The effects of sintering temperature and FA content on the mechanical performance of the ceramics were systematically studied. The phase composition and microstructure of the SFC were characterized using X-ray diffraction and scanning electron microscopy. At 1150 degrees C, an SFC with 30 wt% FA exhibited optimal properties, i.e., a porosity of 64.43%, bulk density of 0.89 g/cm3, and bending strength of 8.34 MPa. As a sintering aid, FA promoted the formation of the mullite phase at low sintering temperatures, which enhanced the anticorrosion and anti-cracking performance of the SFC. Therefore, adding FA to SiC significantly lowers the sintering temperature and reduces the fabrication cost associated with the SFC. Consequently, its commercial application is considerably enhanced.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据