标题
Hydrogen-induced cracking and blistering in steels: A review
作者
关键词
Hydrogen-induced cracking, Corrosion, Hydrogen sulfide environment, Blistering
出版物
Journal of Natural Gas Science and Engineering
Volume 101, Issue -, Pages 104547
出版商
Elsevier BV
发表日期
2022-03-29
DOI
10.1016/j.jngse.2022.104547
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- Microcrack initiation mechanism in hydrogen induced cracking in nickel
- (2021) Noriyuki Takano et al. PHILOSOPHICAL MAGAZINE
- Effect of hydrogen charging time on hydrogen blister and hydrogen-induced cracking of pure iron
- (2021) Xinfeng Li et al. CORROSION SCIENCE
- Crack propagation rate of hydrogen-induced cracking in high sulfur-containing pipelines
- (2021) Shaohua Dong et al. ENGINEERING FAILURE ANALYSIS
- Effects of different cooling rates on the microstructure, crystallographic features, and hydrogen induced cracking of API X80 pipeline steel
- (2021) Mario F.G. Ramirez et al. Journal of Materials Research and Technology-JMR&T
- Effects of thermal spray aluminium coating on SSC and HIC resistance of high strength steel in a sour environment
- (2020) João C.B. Bertoncello et al. SURFACE & COATINGS TECHNOLOGY
- Hydrogen embrittlement in ferritic steels
- (2020) May L. Martin et al. Applied Physics Reviews
- The synergistic action and interplay of hydrogen embrittlement mechanisms in steels and iron: Localized plasticity and decohesion
- (2019) Milos B. Djukic et al. ENGINEERING FRACTURE MECHANICS
- Synchrotron X-ray Laue diffraction study of hydrogen-induced blisters on iron grain boundaries
- (2019) Xuan Tao et al. SCRIPTA MATERIALIA
- Understanding the effect of niobium on hydrogen-induced blistering in pipeline steel: A combined experimental and theoretical study
- (2019) Shiqi Zhang et al. CORROSION SCIENCE
- Effect of Nb on the hydrogen-induced cracking of high-strength low-alloy steel
- (2018) Shiqi Zhang et al. CORROSION SCIENCE
- Hydrogen-enhanced-plasticity mediated decohesion for hydrogen-induced intergranular and “quasi-cleavage” fracture of lath martensitic steels
- (2018) Akihide Nagao et al. JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS
- Failure of electric resistance welded API pipes – Effect of centre line segregation
- (2018) Arnab Karani et al. ENGINEERING FAILURE ANALYSIS
- Enumeration of the hydrogen-enhanced localized plasticity mechanism for hydrogen embrittlement in structural materials
- (2018) May L. Martin et al. ACTA MATERIALIA
- The predominant role of strain-induced vacancies in hydrogen embrittlement of steels: Overview
- (2018) Michihiko Nagumo et al. ACTA MATERIALIA
- A focus on different factors affecting hydrogen induced cracking in oil and natural gas pipeline steel
- (2017) M.A. Mohtadi-Bonab et al. ENGINEERING FAILURE ANALYSIS
- Hydrogen bubble nucleation in α-iron
- (2017) W.T. Geng et al. SCRIPTA MATERIALIA
- Crack and blister initiation and growth in purified iron due to hydrogen loading
- (2016) Marie C. Tiegel et al. ACTA MATERIALIA
- An extensive study of hydrogen-induced cracking susceptibility in an API X60 sour service pipeline steel
- (2016) M.A. Mohtadi-Bonab et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- Novel Cu-bearing high-strength pipeline steels with excellent resistance to hydrogen-induced cracking
- (2016) Xianbo Shi et al. MATERIALS & DESIGN
- The mechanism of failure by hydrogen induced cracking in an acidic environment for API 5L X70 pipeline steel
- (2015) M.A. Mohtadi-Bonab et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- Effect of microstructures and inclusions on hydrogen-induced cracking and blistering of A537 steel
- (2015) X.S. Du et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Critical Assessment 17: Mechanisms of hydrogen induced cracking in pipeline steels
- (2015) K. O. Findley et al. MATERIALS SCIENCE AND TECHNOLOGY
- Three-dimensional imaging of hydrogen blister in iron with neutron tomography
- (2014) Axel Griesche et al. ACTA MATERIALIA
- Evaluation of hydrogen induced cracking behavior of API X70 pipeline steel at different heat treatments
- (2014) M.A. Mohtadi-Bonab et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- Effect of manganese content and microstructure on the susceptibility of X70 pipeline steel to hydrogen cracking
- (2012) D. Hejazi et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Microstructure and Hydrogen-Induced Failure Mechanisms in Fe and Ni Alloy Weldments
- (2012) J. A. Fenske et al. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
- Influence of Ti addition on the hydrogen induced cracking of API 5L X70 hot-rolled pipeline steel in acid sour media
- (2012) Joonoh Moon et al. METALS AND MATERIALS INTERNATIONAL
- Cathodic Induction of Hydrogen Blistering on Carbon Steel in Alkaline Sour Environment
- (2011) M.A. Domínguez-Aguilar et al. CORROSION
- Internal and surface damage of multiphase steels and pure iron after electrochemical hydrogen charging
- (2011) D. Pérez Escobar et al. CORROSION SCIENCE
- On the role of crystallographic texture in mitigating hydrogen-induced cracking in pipeline steels
- (2011) V. Venegas et al. CORROSION SCIENCE
- The experiment research of corrosion behaviour about Ni-based alloys in simulant solution containing H2S/CO2
- (2011) X.H. Zhao et al. ELECTROCHIMICA ACTA
- Hydrogen interaction with multiple traps: Can it be used to mitigate embrittlement?
- (2011) M. Dadfarnia et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- Effects of sulphide ion on the corrosion behaviour of X52 steel in a carbon dioxide environment at temperature 40°C
- (2011) M.C. Fatah et al. MATERIALS CHEMISTRY AND PHYSICS
- Effect of bainitic microstructure on the susceptibility of pipeline steels to hydrogen induced cracking
- (2011) M.A. Arafin et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Degradation of the pipe-steel structure upon long-term operation in contact with a hydrogen sulfide-containing medium
- (2011) V. M. Schastlivtsev et al. PHYSICS OF METALS AND METALLOGRAPHY
- Effect of Microstructure on Hydrogen-Induced Cracking of Linepipe Steels
- (2010) S. U. Koh et al. CORROSION
- The effect of H2S concentration on the corrosion behavior of carbon steel at 90°C
- (2010) Junwen Tang et al. CORROSION SCIENCE
- Comparative assessment of electrochemical hydrogen absorption by pipeline steels with different strength
- (2010) J. Capelle et al. CORROSION SCIENCE
- Investigations of corrosion films formed on API-X52 pipeline steel in acid sour media
- (2010) A. Hernández-Espejel et al. CORROSION SCIENCE
- Hydrogen-induced cracking susceptibility and hydrogen trapping efficiency of different microstructure X80 pipeline steel
- (2010) F. Huang et al. JOURNAL OF MATERIALS SCIENCE
- Hydrogen-Induced Cracking in GMA Welds of Vanadium–Titanium Microalloyed High Strength Steel
- (2010) K. Venkatesan et al. MATERIALS AND MANUFACTURING PROCESSES
- Problems of fracture of metals in hydrogen-sulfide media
- (2010) M. S. Khoma MATERIALS SCIENCE
- Effect of microstructure and inclusions on hydrogen induced cracking susceptibility and hydrogen trapping efficiency of X120 pipeline steel
- (2010) F. Huang et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Film properties and stability influence on impedance distribution during the dissolution process of low-carbon steel exposed to modified alkaline sour environment
- (2009) Homero Castaneda et al. CORROSION SCIENCE
- Formation of hydrogen blister on AZ91 magnesium alloy during cathodic charging
- (2009) Jian Chen et al. CORROSION SCIENCE
- Effect of heat treatment on H2S corrosion of a micro-alloyed C–Mn steel
- (2009) M.A. Lucio-Garcia et al. CORROSION SCIENCE
- Role of microtexture in the interaction and coalescence of hydrogen-induced cracks
- (2009) V. Venegas et al. CORROSION SCIENCE
- Hydrogen induced cracking (HIC) testing of low alloy steel in sour environment: Impact of time of exposure on the extent of damage
- (2009) Jean Kittel et al. CORROSION SCIENCE
- Effects of hydrogen-charging on the susceptibility of X100 pipeline steel to hydrogen-induced cracking
- (2009) C.F. Dong et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- Hydrogen-induced cracking and healing behaviour of X70 steel
- (2009) C.F. Dong et al. JOURNAL OF ALLOYS AND COMPOUNDS
- Metallurgical factors in stress corrosion cracking (SCC) and hydrogen-induced cracking (HIC)
- (2009) M. Elboujdaini et al. JOURNAL OF SOLID STATE ELECTROCHEMISTRY
- A statistical, physical-based, micro-mechanical model of hydrogen-induced intergranular fracture in steel
- (2009) P. Novak et al. JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS
- Relationship between hydrogen-induced cracking and type I sulfide stress cracking of high-strength linepipe steel
- (2009) Wan Keun Kim et al. SCRIPTA MATERIALIA
- Effect of microstructure on the hydrogen trapping efficiency and hydrogen induced cracking of linepipe steel
- (2008) Gyu Tae Park et al. CORROSION SCIENCE
- Effect of environmental and metallurgical factors on hydrogen induced cracking of HSLA steels
- (2008) Wan Keun Kim et al. CORROSION SCIENCE
- Effects of alloying elements and microstructure on the susceptibility of the welded HSLA steel to hydrogen-induced cracking and sulfide stress cracking
- (2008) B. Beidokhti et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
Create your own webinar
Interested in hosting your own webinar? Check the schedule and propose your idea to the Peeref Content Team.
Create NowAsk a Question. Answer a Question.
Quickly pose questions to the entire community. Debate answers and get clarity on the most important issues facing researchers.
Get Started