Investigation of microstructural changes of Pt-Al-7% YSZ coating during high-temperature hot corrosion and its effect on tensile properties of coated Rene-80 superalloy at 950 °C
出版年份 2022 全文链接
标题
Investigation of microstructural changes of Pt-Al-7% YSZ coating during high-temperature hot corrosion and its effect on tensile properties of coated Rene-80 superalloy at 950 °C
作者
关键词
Rene-80, Pt-Al-7%YSZ, Tensile properties, Hot corrosion, Microstructure
出版物
SURFACE & COATINGS TECHNOLOGY
Volume 439, Issue -, Pages 128461
出版商
Elsevier BV
发表日期
2022-04-22
DOI
10.1016/j.surfcoat.2022.128461
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- The evaluation of oxide scale formation during hot corrosion of Rene-80 superalloy under thermal shock at different dwell times
- (2021) Arman Rabieifar et al. CORROSION ENGINEERING SCIENCE AND TECHNOLOGY
- High Temperature Micromechanical Behavior of a Pt-Modified Nickel Aluminide Bond-Coating and of Its Interdiffusion Zone with the Superalloy Substrate
- (2020) Damien Texier et al. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
- Microstructural evolution and cyclic oxidation of Pt-Al-YSZ coating under thermal shock
- (2020) Arman Rabieifar et al. Materials Research Express
- Effect of Pt-Al bond-coat on the tensile deformation and fracture behaviors of a second-generation SX Ni-based superalloy at elevated temperatures
- (2020) X.P. Tao et al. SURFACE & COATINGS TECHNOLOGY
- Microstructural analysis after furnace cyclic testing of pre-oxidized ReneN5/(Ni,Pt)Al/7YSZ thermal barrier coatings
- (2020) A.G. Mora-García et al. SURFACE & COATINGS TECHNOLOGY
- Mechanical behaviour of conventional, Pt- and Pt/Ir-modified NiAl diffusion coatings after thermocyclic exposure at 1100°C
- (2019) Ceyhun Oskay et al. MATERIALS AT HIGH TEMPERATURES
- Failure and life evaluation of EB-PVD thermal barrier coatings using temperature-process-dependent model parameters
- (2019) B.C. Zhang et al. CORROSION SCIENCE
- Oxidation and concomitant effects on the microstructure and high temperature tensile properties of a DS Ni-base superalloy applied with different thicknesses of Pt-aluminide (PtAl) bond coat
- (2019) Chandrakant Parlikar et al. SURFACE & COATINGS TECHNOLOGY
- Thickness apropos stoichiometry in Pt-aluminide (PtAl) coating: Implications on the tensile properties of a directionally solidified Ni-base superalloy
- (2017) Chandrakant Parlikar et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Comparative tensile behavior of freestanding γ-γ′ and β-(Ni,Pt)Al bond coats and effect on tensile properties of coated superalloy
- (2017) Md Zafir Alam et al. MATERIALS & DESIGN
- Progress update on failure mechanisms of advanced thermal barrier coatings: A review
- (2016) Vijay Kumar et al. PROGRESS IN ORGANIC COATINGS
- Additive Manufacturing and Characterization of René 80 Superalloy Processed Through Scanning Laser Epitaxy for Turbine Engine Hot-Section Component Repair
- (2015) Ranadip Acharya et al. ADVANCED ENGINEERING MATERIALS
- Propagation feature of cracks in plasma-sprayed YSZ coatings under gradient thermal cycling
- (2015) Hui Dong et al. CERAMICS INTERNATIONAL
- In-situ study of microscale fracture of diffusion aluminide bond coats: Effect of platinum
- (2015) Balila Nagamani Jaya et al. JOURNAL OF MATERIALS RESEARCH
- Hot Corrosion of Yttria-Stabilized Zirconia Coating, in a Mixture of Sodium Sulfate and Vanadium Oxide at 950 °C
- (2015) Imran Nazir Qureshi et al. JOURNAL OF THERMAL SPRAY TECHNOLOGY
- Effect of Pt–aluminide bond coat on tensile and creep behavior of a nickel-base single crystal superalloy
- (2015) Chandrakant Parlikar et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Micromechanisms of fracture and strengthening in free-standing Pt-aluminide bond coats under tensile loading
- (2014) Md. Zafir Alam et al. ACTA MATERIALIA
- Comparison of oxidation performance of two nickel base superalloys for turbine applications
- (2014) B. G. Cade et al. CANADIAN METALLURGICAL QUARTERLY
- Thermal shock behavior of platinum aluminide bond coat/electron beam-physical vapor deposited thermal barrier coatings
- (2014) Zhenhua Xu et al. JOURNAL OF ALLOYS AND COMPOUNDS
- Investigation of three steps of hot corrosion process in Y2O3 stabilized ZrO2 coatings including nano zones
- (2014) Mohammadreza Daroonparvar et al. JOURNAL OF RARE EARTHS
- An investigation on hot corrosion behavior of YSZ-Ta2O5 in Na2SO4+V2O5 salt at 1100°C
- (2013) M.H. Habibi et al. CORROSION SCIENCE
- Effect of substrate curvature on residual stresses and failure modes of an air plasma sprayed thermal barrier coating system
- (2013) D. Liu et al. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
- Evolution of Lamellar Interface Cracks During Isothermal Cyclic Test of Plasma-Sprayed 8YSZ Coating with a Columnar-Structured YSZ Interlayer
- (2013) Chang-Jiu Li et al. JOURNAL OF THERMAL SPRAY TECHNOLOGY
- Cohesive zone modelling of thermal barrier coatings interfacial properties based on three-dimensional observations and mechanical testing
- (2013) R. Soulignac et al. SURFACE & COATINGS TECHNOLOGY
- Tensile behavior of a free-standing Pt-aluminide (PtAl) bond coat
- (2012) Md Zafir Alam et al. ACTA MATERIALIA
- Evaluation of hot corrosion behavior of plasma sprayed ceria and yttria stabilized zirconia thermal barrier coatings in the presence of Na2SO4+V2O5 molten salt
- (2012) Raheleh Ahmadi-Pidani et al. CERAMICS INTERNATIONAL
- Microstructural evolution of Pt-aluminide coating influenced by cycle oxidation service conditions
- (2012) M.A. González et al. ENGINEERING FAILURE ANALYSIS
- Evolution of hot corrosion resistance of YSZ, Gd2Zr2O7, and Gd2Zr2O7+YSZ composite thermal barrier coatings in Na2SO4+V2O5 at 1050°C
- (2012) M.H. Habibi et al. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
- Effects of heat treatments on the microstructure and mechanical properties of Rene 80
- (2012) Caixiong Yang et al. MATERIALS & DESIGN
- Environmental degradation of thermal-barrier coatings by molten deposits
- (2012) Carlos G. Levi et al. MRS BULLETIN
- Multifunctional coating interlayers for thermal-barrier systems
- (2012) T.M. Pollock et al. MRS BULLETIN
- Hot corrosion of a novel (Ni,Co)O/(Ni,Co)Fe2O4 composite coating thermally converted from an electrodeposited Ni–Co–Fe2O3 composite coating
- (2011) Li Ma et al. CORROSION SCIENCE
- Evaluation of microstructural evolution of thermal barrier coatings exposed to Na2SO4 using impedance spectroscopy
- (2011) Hui Huang et al. CORROSION SCIENCE
- Hot corrosion of a novel NiO/NiFe2O4 composite coating thermally converted from the electroplated Ni–Fe alloy
- (2011) Li Ma et al. CORROSION SCIENCE
- Determining a critical strain for APS thermal barrier coatings under service relevant loading conditions
- (2011) H. Aleksanoglu et al. INTERNATIONAL JOURNAL OF FATIGUE
- Oxidation resistance of YSZ-alumina composites compared to normal YSZ TBC coatings at 1100°C
- (2011) A. Keyvani et al. JOURNAL OF ALLOYS AND COMPOUNDS
- Effect of Cyclic Oxidation Exposure on Tensile Properties of a Pt-Aluminide Bond-Coated Ni-Base Superalloy
- (2011) Md. Zafir Alam et al. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
- Study of brittle-to-ductile-transition in Pt-aluminide bond coat using micro-tensile testing method
- (2011) Md Zafir Alam et al. TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS
- On the interfacial degradation mechanisms of thermal barrier coating systems: Effects of bond coat composition
- (2010) R.T. Wu et al. ACTA MATERIALIA
- Coarsening of a multimodal nickel-base superalloy
- (2010) James Coakley et al. ACTA MATERIALIA
- Evaluation of ductile–brittle transition temperature (DBTT) of aluminide bond coats by micro-tensile test method
- (2010) Md. Zafir Alam et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Determination of the ductile to brittle temperature transition of aluminide coatings and its influence on the mechanical behavior of coated specimens
- (2010) Sebastien Dryepondt et al. SURFACE & COATINGS TECHNOLOGY
- The influence of bondcoat and topcoat mechanical properties on stress development in thermal barrier coating systems
- (2009) E.P. Busso et al. ACTA MATERIALIA
- Creep Life Prediction of Thermally Exposed Rene 80 Superalloy
- (2009) M. Aghaie-Khafri et al. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
- Mechanism of failure in a free-standing Pt–aluminide bond coat during tensile testing at room temperature
- (2009) Md. Zafir Alam et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Mechanical Properties of Uncoated and Aluminide-Coated René 80
- (2009) Kh. Rahmani et al. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
- The effect of Pt contents on the surface morphologies of Pt-modified aluminide coating
- (2009) S.J. Hong et al. SURFACE & COATINGS TECHNOLOGY
- Rumpling of CVD (Ni,Pt)Al diffusion coatings under intermediate temperature cycling
- (2009) V.K. Tolpygo et al. SURFACE & COATINGS TECHNOLOGY
- The influence of oxides on the performance of advanced gas turbines
- (2008) A.G. Evans et al. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
- Damage mechanisms and lifetime behavior of plasma sprayed thermal barrier coating systems for gas turbines—Part I: Experiments
- (2008) O. Trunova et al. SURFACE & COATINGS TECHNOLOGY
- Damage mechanisms and lifetime behavior of plasma-sprayed thermal barrier coating systems for gas turbines — Part II: Modeling
- (2008) Tilmann Beck et al. SURFACE & COATINGS TECHNOLOGY
- Influence of aluminide diffusion coating on the tensile properties of the Ni-base superalloy René 80
- (2007) Kh. Rahmani et al. SURFACE & COATINGS TECHNOLOGY
Find Funding. Review Successful Grants.
Explore over 25,000 new funding opportunities and over 6,000,000 successful grants.
ExploreAsk a Question. Answer a Question.
Quickly pose questions to the entire community. Debate answers and get clarity on the most important issues facing researchers.
Get Started