Combined evaluation of Young modulus and fracture toughness in small specimens of fine grained nuclear graphite using 3D image analysis
出版年份 2022 全文链接
标题
Combined evaluation of Young modulus and fracture toughness in small specimens of fine grained nuclear graphite using 3D image analysis
作者
关键词
Graphite, Digital volume correlation, Double cleavage drilled compression, Strain energy release rate, Fracture toughness
出版物
JOURNAL OF NUCLEAR MATERIALS
Volume 563, Issue -, Pages 153642
出版商
Elsevier BV
发表日期
2022-03-10
DOI
10.1016/j.jnucmat.2022.153642
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- 4D synchrotron X-ray microtomography of fracture in nuclear graphite after neutron irradiation and radiolytic oxidation
- (2020) J. Wade-Zhu et al. CARBON
- Assessment of the fracture toughness of neutron-irradiated nuclear graphite by 3D analysis of the crack displacement field
- (2020) Xiaochao Jin et al. CARBON
- Inverse identification of graphite damage properties under complex stress states
- (2019) Guangyan Liu et al. MATERIALS & DESIGN
- Measuring the fracture properties of irradiated reactor core graphite
- (2018) Athanasia Tzelepi et al. JOURNAL OF NUCLEAR MATERIALS
- Fracture behavior of nuclear graphite under three-point bending tests
- (2017) H.H.N. Chen et al. ENGINEERING FRACTURE MECHANICS
- J-Integral Calculation by Finite Element Processing of Measured Full-Field Surface Displacements
- (2017) S.M. Barhli et al. EXPERIMENTAL MECHANICS
- An autonomous surface discontinuity detection and quantification method by digital image correlation and phase congruency
- (2017) A.F. Cinar et al. OPTICS AND LASERS IN ENGINEERING
- In situ measurement of the strains within a mechanically loaded polygranular graphite
- (2016) T.J. Marrow et al. CARBON
- Yield behavior beneath hardness indentations in ductile metals, measured by three-dimensional computed X-ray tomography and digital volume correlation
- (2015) M. Mostafavi et al. ACTA MATERIALIA
- Spatial variability in the coefficient of thermal expansion induces pre-service stresses in computer models of virgin Gilsocarbon bricks
- (2015) José David Arregui-Mena et al. JOURNAL OF NUCLEAR MATERIALS
- Failure prediction of full-size reactor components from tensile specimen data on NBG-18 nuclear graphite
- (2015) Michael P. Hindley et al. NUCLEAR ENGINEERING AND DESIGN
- Investigation on structural integrity of graphite component during high temperature 950 °C continuous operation of HTTR
- (2014) Junya Sumita et al. JOURNAL OF NUCLEAR SCIENCE AND TECHNOLOGY
- Constitutive modeling and finite element procedure development for stress analysis of prismatic high temperature gas cooled reactor graphite core components
- (2013) Subhasish Mohanty et al. NUCLEAR ENGINEERING AND DESIGN
- A model of Young’s modulus for Gilsocarbon graphites irradiated in oxidising environments
- (2012) Ernest D. Eason et al. JOURNAL OF NUCLEAR MATERIALS
- Failure probability study of HTR graphite component using microstructure-based model
- (2012) Suyuan Yu et al. NUCLEAR ENGINEERING AND DESIGN
- Damage, crack growth and fracture characteristics of nuclear grade graphite using the Double Torsion technique
- (2011) T.H. Becker et al. JOURNAL OF NUCLEAR MATERIALS
- Crack opening profile in DCDC specimen
- (2009) Gaël Pallares et al. INTERNATIONAL JOURNAL OF FRACTURE
- Microstructural scale strain localisation in nuclear graphite
- (2008) M.R. Joyce et al. JOURNAL OF NUCLEAR MATERIALS
- Graphite irradiation testing for HTR technology at the High Flux Reactor in Petten
- (2008) J.A. Vreeling et al. JOURNAL OF NUCLEAR MATERIALS
- Characterization of heterogeneity and nonlinearity in material properties of nuclear graphite using an inverse method
- (2008) Lianshan Lin et al. JOURNAL OF NUCLEAR MATERIALS
- Estimation of graphite density and mechanical strength variation of VHTR during air-ingress accident
- (2007) Eung Soo Kim et al. NUCLEAR ENGINEERING AND DESIGN
Discover Peeref hubs
Discuss science. Find collaborators. Network.
Join a conversationBecome a Peeref-certified reviewer
The Peeref Institute provides free reviewer training that teaches the core competencies of the academic peer review process.
Get Started