JOURNAL OF ALLOYS AND COMPOUNDS
卷 669, 期 -, 页码 1-7出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2016.01.235
关键词
Inorganic materials; Precipitation; Scanning electron microscopy; X-ray diffraction; Ionic conduction
资金
- Special Fund for Basic Scientific Research of Central Colleges, South-Central University for Nationalities [CZW15090]
In this present work, chemical precipitation method was employed for preparing cerium oxide. XRD, SEM, TEM, TGA/DTA and BET were used to investigate the structure, shape and formation mechanism, respectively. No impurities were detected. It was found that alcohol had obvious effection on the growth of the final sample. The shape of the precursor was retained after calcined at 500 degrees C. This result led to thepossibility of an easy scale up to a commercial process. EIS and charge-discharge tests were carried out by using the as-prepared CeO2 as an anode material for lithium ion batteries. Specially, the initial discharge specific capacity of the rhombus CeO2 was about 529 mAh g(-1) and stabilized reversibly at about 374 mAh g(-1) after 50 cycles. It showed a promising usage as anode materials in lithium ion battery. (C) 2016 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据