期刊
INTERNATIONAL JOURNAL OF FATIGUE
卷 156, 期 -, 页码 -出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ijfatigue.2021.106637
关键词
Multiaxial fatigue; Loading path non-proportionality; Local misorientation; Dislocation substructure; Life prediction
资金
- National Natural Science Foundation of China [11772219, 12011540001]
This work studied the low cycle fatigue behavior of 316LN stainless steel at high temperature, and found the influence of loading path non-proportionality and the difference of crack initiation and growth modes. It proposed a method to modify the life prediction model for more accurate results.
This work studied the uniaxial, torsional and multiaxial low cycle fatigue behavior of 316LN stainless steel at 550 degrees C. Results show that the normalized kernel average misorientation value can be used to describe the loading path non-proportionality quantitatively. The formation of equiaxed and small-sized dislocation cells leads to the occurrence of continuously cyclic hardening under circular loading path. The crack initiation and early crack growth is dominated by intergranular mode in uniaxial test, whereas the transgranular cracking is observed in multiaxial test. Moreover, a weighting factor, evaluating the contribution of shear fatigue damage to the total multiaxial damage is proposed to modify the damage parameter of Chen-Xu-Huang (CXH) life prediction model, which enables all life data falling into the scatter band of 1.5.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据