Experimental and numerical analysis of wrinkles influence on damage mechanisms and strength of L-Shape cross-ply composite beams
出版年份 2022 全文链接
标题
Experimental and numerical analysis of wrinkles influence on damage mechanisms and strength of L-Shape cross-ply composite beams
作者
关键词
Defects, Delamination, Matrix cracking, Finite element analysis (FEA), In-situ FE mesh
出版物
COMPOSITES SCIENCE AND TECHNOLOGY
Volume 223, Issue -, Pages 109420
出版商
Elsevier BV
发表日期
2022-03-28
DOI
10.1016/j.compscitech.2022.109420
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- Continuum and cohesive zone damage models to study intra/inter-laminar failure of curved composite laminates under four-point bending
- (2020) Lala Bahadur Andraju et al. COMPOSITE STRUCTURES
- Effect of out-of-plane wrinkles in curved multi-directional carbon/epoxy laminates
- (2020) Xiaodong Xu et al. COMPOSITES SCIENCE AND TECHNOLOGY
- Experimental and three-dimensional numerical investigation of matrix cracking and delamination interaction with edge effect of curved composite laminates
- (2019) Dongfeng Cao et al. COMPOSITE STRUCTURES
- Experimental and numerical analysis of unfolding failure of L-shaped CFRP specimens
- (2019) P. Journoud et al. COMPOSITE STRUCTURES
- Computational investigation of both intra-laminar matrix cracking and inter-laminar delamination of curved composite components with cohesive elements
- (2018) Dongfeng Cao et al. COMPOSITE STRUCTURES
- Delamination analysis of multi-angle composite curved beams using an out-of-autoclave material
- (2018) Khanh-Hung Nguyen et al. COMPOSITE STRUCTURES
- Failure load analysis of C-shaped composite beams using a cohesive zone model
- (2018) Viet-Hoai Truong et al. COMPOSITE STRUCTURES
- Competing mechanisms in the unfolding failure in composite laminates
- (2018) J.M. González-Cantero et al. COMPOSITES SCIENCE AND TECHNOLOGY
- Resin treatment of free edges to aid certification of through thickness laminate strength
- (2016) Timothy A. Fletcher et al. COMPOSITE STRUCTURES
- Tensile failure of laminates containing an embedded wrinkle; numerical and experimental study
- (2015) Supratik Mukhopadhyay et al. COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING
- Compressive failure of laminates containing an embedded wrinkle; experimental and numerical study
- (2015) Supratik Mukhopadhyay et al. COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING
- Methods for assessment of interlaminar tensile strength of composite materials
- (2014) Andrew Makeev et al. JOURNAL OF COMPOSITE MATERIALS
- Life cycle monitoring and advanced quality assurance of L-shaped composite corner part using embedded fiber-optic sensor
- (2013) Shu Minakuchi et al. COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING
- A new mechanism for the formation of ply wrinkles due to shear between plies
- (2013) James S. Lightfoot et al. COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING
- Effects of defects on interlaminar tensile fatigue behavior of carbon/epoxy composites
- (2013) Guillaume Seon et al. COMPOSITES SCIENCE AND TECHNOLOGY
- Structural analysis of composites with porosity defects based on X-ray computed tomography
- (2013) Yuri Nikishkov et al. JOURNAL OF COMPOSITE MATERIALS
- Experimental investigation on deformation and strength of carbon/epoxy laminated curved beams
- (2012) Wenfeng Hao et al. POLYMER TESTING
- Numerical simulation of delamination in laminated composite components – A combination of a strength criterion and fracture mechanics
- (2009) G. Wimmer et al. COMPOSITES PART B-ENGINEERING
Find the ideal target journal for your manuscript
Explore over 38,000 international journals covering a vast array of academic fields.
SearchAsk a Question. Answer a Question.
Quickly pose questions to the entire community. Debate answers and get clarity on the most important issues facing researchers.
Get Started