期刊
POLYMER ENGINEERING AND SCIENCE
卷 61, 期 7, 页码 2033-2042出版社
WILEY
DOI: 10.1002/pen.25719
关键词
mechanical properties; polyethylene; polyurethane elastomers; self-lubrication; surfaces; tribology
资金
- Priority Academic Program Development of Jiangsu Higher Education Institutions
- Government of Jiangsu Province [KYCX18_2245, KYCX19_1597]
Surface-modified UHMWPE powder can be evenly dispersed in polyurethane, enhancing its internal stress and mechanical properties, while also improving wear resistance and lubricating performance of the elastomer.
Ultra-high molecular weight polyethylene (UHMWPE) powder was modified by surface treatment technology, then its wettability, dispersibility, mechanical, and tribological properties in polyurethane elastomer were studied. The testing results showed that after surface treatment, UHMWPE powder could infiltrate and disperse evenly in polyurethane, and build micro cross-link with the contact surface of polymer substrate, which is conducive to enhancing the internal stress of polymer and improving the mechanical properties. With a small amount of modified UHMWPE being added into the casting polyurethane (CPU) elastomer, the right-angled tearing strength increases and the abrasion loss decreases. Moreover, the elastomer surface self-lubricating performance of CPU compounding with modified UHMWPE is enhanced: compared with the neat CPU sample, the average friction coefficient of the CPU samples with 5%, 10%, and 15% of modified UHMWPE is reduced by 46.3%, 41.5%, and 39.0%, respectively, and the surface wear resistance is improved; under the high-load working condition, the CPU elastomer with 5% of modified UHMWPE has the optimal tribological performance.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据