Evaluation of strength and microstructure of welded pipes with wall lamination
作者
关键词
Lamination, Weld, Stress-strain diagram, Defects of rolled metal, Metallography
出版物
ENGINEERING FAILURE ANALYSIS
Volume 122, Issue -, Pages 105235
出版商
Elsevier BV
发表日期
2021-01-14
DOI
10.1016/j.engfailanal.2021.105235
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- Application of USCCD on Girth Weld Defect Detection of Oil Pipelines
- (2020) L. S. Dai et al. Applied Sciences-Basel
- Mechanical Properties of Gas Main Steels after Long-Term Operation and Peculiarities of Their Fracture Surface Morphology
- (2019) Volodymyr Hutsaylyuk et al. Materials
- Fatigue Testing of Pipeline Welds and Heat-Affected Zones in Pressurized Hydrogen Gas
- (2019) Elizabeth S. Drexler et al. JOURNAL OF RESEARCH OF THE NATIONAL INSTITUTE OF STANDARDS AND TECHNOLOGY
- Morphology and development dynamics of rolled steel products manufacturing defects during long-term operation in main gas pipelines
- (2019) Dmitrii Zhukov et al. ENGINEERING FAILURE ANALYSIS
- Explosion in gas pipeline: Witnesses' perceptions and expert analyses' results
- (2019) Pablo G. Cirimello et al. ENGINEERING FAILURE ANALYSIS
- A strain-controlled fracture assessment for submarine thin-walled pipes with V-groove welds and circumferential embedded cracks
- (2019) Xiaoxin Zhao et al. THIN-WALLED STRUCTURES
- Failure analysis of a natural gas pipeline
- (2018) Hadi Shabani et al. ENGINEERING FAILURE ANALYSIS
- Fatigue crack growth rates of X100 steel welds in high pressure hydrogen gas considering residual stress effects
- (2018) Joseph A. Ronevich et al. ENGINEERING FRACTURE MECHANICS
- Contribution of finite element analyses to crack-like flaw assessments in a gas pipeline
- (2018) Thibault Jacquemin et al. INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING
- Analysis of the Causes of Failure of a Pipeline Welded Joint
- (2018) Yu. A. Chirkov et al. METAL SCIENCE AND HEAT TREATMENT
- Analysis of 3D Planar Laminations in a Welded Section of API 5L X52 Applying the Finite Element Method
- (2018) Martin. J. Fernández-Cueto et al. Soldagem & Inspecao
- Modelling 3D interaction limits of inclined stress corrosion cracking in pressurised gas pipelines
- (2018) James Griggs et al. INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING
- Assessment of yield strength mismatch in X80 pipeline steel welds using instrumented indentation
- (2018) A.R.H. Midawi et al. INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING
- Welding effect on tensile strength of grade S690Q steel butt joint
- (2018) Cheng Chen et al. JOURNAL OF CONSTRUCTIONAL STEEL RESEARCH
- Influence of morphological characteristics on the mechanical properties and failure mechanisms of legacy butt welds
- (2018) Bo-Tong Zheng et al. CONSTRUCTION AND BUILDING MATERIALS
- Analysis and mechanical properties characterization of operated gas main elbow with hydrogen assisted large-scale delamination
- (2017) H. Nykyforchyn et al. ENGINEERING FAILURE ANALYSIS
- Microalloyed steel welds by HF-ERW technique: Novel PWHT cycles, microstructure evolution and mechanical properties enhancement
- (2017) Gholamreza Khalaj et al. INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING
- Integrity assessment of API X70 pipe with corroded girth and seam welds via numerical simulation and burst test experiments
- (2016) Kyu Jung Yeom et al. ENGINEERING FAILURE ANALYSIS
- Defects detection of gas pipeline near the welds based on self quotient image and discrete cosine transform
- (2016) Hyung Min Kim et al. RUSSIAN JOURNAL OF NONDESTRUCTIVE TESTING
- Literature Review: Theory and Application of In-Line Inspection Technologies for Oil and Gas Pipeline Girth Weld Defection
- (2016) Qingshan Feng et al. SENSORS
- Fracture assessments of clad pipe girth welds incorporating improved crack driving force solutions
- (2015) Rodolfo F. Souza et al. ENGINEERING FRACTURE MECHANICS
- Hydrogen embrittlement susceptibility of a weld simulated X70 heat affected zone under H2 pressure
- (2014) A. Alvaro et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Assessment on failure pressure of high strength pipeline with corrosion defects
- (2013) Bin Ma et al. ENGINEERING FAILURE ANALYSIS
Find the ideal target journal for your manuscript
Explore over 38,000 international journals covering a vast array of academic fields.
SearchCreate your own webinar
Interested in hosting your own webinar? Check the schedule and propose your idea to the Peeref Content Team.
Create Now