MATERIALS RESEARCH BULLETIN
卷 133, 期 -, 页码 -出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.materresbull.2020.111057
关键词
Gallium doping; green TiO2; plant waste; photocatalysis; MB; phenol
Green and porous Ga3+ doped TiO2 nanostructures were successfully prepared using plant waste extract and ultrasonic irradiation, exhibiting enhanced photocatalytic activity. The incorporation of Ga3+ ions in TiO2 crystal was successful, with the best result obtained for 0.5 wt.% of Ga.
Green and porous Ga3+ doped TiO2 nanostructures have been successfully prepared using plant waste extract and ultrasonic irradiation. The produced nanomaterials have been investigated using XRD, Raman, FTIR, SEM, TEM, BET and XPS. The results revealed the formation of micro-/macro-porous TiO2 anatase with high surface area compared to pure TiO2 prepared under identical conditions. All results revealed the successful incorporation of Ga3+ ions in the TiO2 crystal at all gallium ratio while XPS results showed the formation of Ga2O3 at high gallium concentration (5 and 10 wt. %). The effect of Ga doping was found to greatly enhance the photocatalytic activity of TiO2 for MB and phenol degradation with best result obtained for 0.5 wt. % of Ga.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据