Laser shock peening-induced surface gradient stress distribution and extension mechanism in corrosion fatigue life of AISI 420 stainless steel
出版年份 2020 全文链接
标题
Laser shock peening-induced surface gradient stress distribution and extension mechanism in corrosion fatigue life of AISI 420 stainless steel
作者
关键词
Laser shock peening, Gradient surface stress distribution, Compressive residual stress, Martensitic stainless steel, Corrosion fatigue crack rate, NaCl solution
出版物
CORROSION SCIENCE
Volume 177, Issue -, Pages 109027
出版商
Elsevier BV
发表日期
2020-09-25
DOI
10.1016/j.corsci.2020.109027
参考文献
相关参考文献
注意：仅列出部分参考文献，下载原文获取全部文献信息。- Effect of grain boundary engineering on corrosion fatigue behavior of 316LN stainless steel in borated and lithiated high-temperature water
- (2019) Jun Gao et al. CORROSION SCIENCE
- Electrochemical and corrosion study of as-cast NixAly intermetallic alloys: Influence of alloy composition and electrolyte pH
- (2019) Birhan Sefer et al. CORROSION SCIENCE
- Uncoupling the effects of strain rate and adiabatic heating on strain induced martensitic phase transformations in a metastable austenitic steel
- (2019) N.I. Vázquez-Fernández et al. ACTA MATERIALIA
- High-performance integrated additive manufacturing with laser shock peening –induced microstructural evolution and improvement in mechanical properties of Ti6Al4V alloy components
- (2019) Jinzhong Lu et al. INTERNATIONAL JOURNAL OF MACHINE TOOLS & MANUFACTURE
- Do corrosion pits eliminate the benefit of shot-peening?
- (2018) A. Turnbull et al. INTERNATIONAL JOURNAL OF FATIGUE
- Surface nanocrystallization of 17-4 precipitation-hardening stainless steel subjected to ultrasonic surface rolling process
- (2018) Dan Liu et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Microstructure modification and mechanical property improvement of reduced activation ferritic/martensitic steel by severe plastic deformation
- (2018) Xiaojie Jin et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Improvement of corrosion resistance of AA2024-T3 using femtosecond laser peening without protective and confining medium
- (2018) Uroš Trdan et al. CORROSION SCIENCE
- Nanoscale precipitation and its influence on strengthening mechanisms in an ultra-high strength low-carbon steel
- (2018) S.S. Xu et al. INTERNATIONAL JOURNAL OF PLASTICITY
- Microstructure evolution in Ti64 subjected to laser-assisted ultrasonic nanocrystal surface modification
- (2018) Jun Liu et al. INTERNATIONAL JOURNAL OF MACHINE TOOLS & MANUFACTURE
- Effect of alternate corrosion factors on multiaxial low-cycle fatigue life of 2024-T4 aluminum alloy
- (2018) Yajun Chen et al. JOURNAL OF ALLOYS AND COMPOUNDS
- Study on the effect of multiple laser shock peening on residual stress and microstructural changes in modified 9Cr-1Mo (P91) steel
- (2018) Arun Kumar Rai et al. SURFACE & COATINGS TECHNOLOGY
- Ultrahigh-strength low carbon steel obtained from the martensitic state via high pressure torsion
- (2018) T. Müller et al. ACTA MATERIALIA
- Microstructural evolution in the welding zone of laser shock peened 316L stainless steel tube
- (2017) J. Z. Lu et al. JOURNAL OF LASER APPLICATIONS
- Effect of Silicon Content on Carbide Precipitation and Low-Temperature Toughness of Pressure Vessel Steels
- (2017) L. H. Ruan et al. METAL SCIENCE AND HEAT TREATMENT
- Electrochemical and pitting corrosion resistance of AISI 4145 steel subjected to massive laser shock peening treatment with different coverage layers
- (2017) J.Z. Lu et al. OPTICS AND LASER TECHNOLOGY
- Microstructure and surface properties of 17-4PH stainless steel by ultrasonic surface rolling technology
- (2017) Qinglong Zhang et al. SURFACE & COATINGS TECHNOLOGY
- Effect of quenching and partitioning on the microstructure evolution and electrochemical properties of a martensitic stainless steel
- (2016) Si-Yuan Lu et al. CORROSION SCIENCE
- Effects of laser shock processing on high cycle fatigue crack growth rate and fracture toughness of aluminium alloy 6082-T651
- (2016) Zoran Bergant et al. INTERNATIONAL JOURNAL OF FATIGUE
- Effect of laser shock peening on microstructure and fatigue crack growth rate of AZ31B magnesium alloy
- (2016) Mao-Zhong Ge et al. JOURNAL OF ALLOYS AND COMPOUNDS
- Morphology, crystallography, and crack paths of tempered lath martensite in a medium-carbon low-alloy steel
- (2016) Chengduo Wang et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Effect of laser peening with different energies on fatigue fracture evolution of 6061-T6 aluminum alloy
- (2016) J. Sheng et al. OPTICS AND LASER TECHNOLOGY
- Formation mechanisms of white layers induced by hard turning of AISI 52100 steel
- (2015) S.B. Hosseini et al. ACTA MATERIALIA
- Fatigue behaviors of AISI 316L stainless steel with a gradient nanostructured surface layer
- (2015) H.W. Huang et al. ACTA MATERIALIA
- Effects of laser shock peening on SCC behavior of Alloy 600 in tetrathionate solution
- (2015) Abhishek Telang et al. CORROSION SCIENCE
- On the influence of laser peening with different coverage areas on fatigue response and fracture behavior of Ti–6Al–4V alloy
- (2015) S. Huang et al. ENGINEERING FRACTURE MECHANICS
- Effect of advancing direction on fatigue life of 316L stainless steel specimens treated by double-sided laser shock peening
- (2015) C. Correa et al. INTERNATIONAL JOURNAL OF FATIGUE
- Corrosion fatigue crack growth behavior of oil-grade nickel-base alloy 718. Part 1: Effect of corrosive environment
- (2014) Ting Chen et al. CORROSION SCIENCE
- SEM/EDS characterization of laser shock peening effect on localized corrosion of Al alloy in a near natural chloride environment
- (2014) Uroš Trdan et al. CORROSION SCIENCE
- Corrosion and metallurgical investigation of two supermartensitic stainless steels for oil and gas environments
- (2014) Thiago J. Mesquita et al. CORROSION SCIENCE
- The effect of preheat & post weld heat treatment on the laser weldability of AISI 420 martensitic stainless steel
- (2014) Ceyhun Köse et al. MATERIALS & DESIGN
- Laser shock peening of steam turbine blade for enhanced service life
- (2014) R SUNDAR et al. PRAMANA-JOURNAL OF PHYSICS
- Characterization of the Nano-Scale Surface Layer of a Tempered Martensitic Steel Synthesized by Ultrasonic Nanocrystalline Surface Modification Treatment
- (2014) Yinsheng He et al. Science of Advanced Materials
- Corrosion behaviour of AISI 304 stainless steel subjected to massive laser shock peening impacts with different pulse energies
- (2013) J.Z. Lu et al. CORROSION SCIENCE
- Effects of laser energy on fatigue crack growth properties of 6061-T6 aluminum alloy subjected to multiple laser peening
- (2013) S. Huang et al. ENGINEERING FRACTURE MECHANICS
- Studies towards development of laser peening technology for martensitic stainless steel and titanium alloys for steam turbine applications
- (2013) B.K. Pant et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Effects of laser peening on residual stresses and fatigue crack growth properties of Ti–6Al–4V titanium alloy
- (2013) J.Z. Zhou et al. OPTICS AND LASERS IN ENGINEERING
- Surface textural features and its formation process of AISI 304 stainless steel subjected to massive LSP impacts
- (2013) K.Y. Luo et al. OPTICS AND LASERS IN ENGINEERING
- Electrochemical short crack effect in environmentally assisted cracking of a steam turbine blade steel
- (2012) A. Turnbull et al. CORROSION SCIENCE
- Evaluation of corrosion resistance of AA6082-T651 aluminium alloy after laser shock peening by means of cyclic polarisation and ElS methods
- (2012) Uroš Trdan et al. CORROSION SCIENCE
- Effects of laser peening on stress corrosion cracking (SCC) of ANSI 304 austenitic stainless steel
- (2012) J.Z. Lu et al. CORROSION SCIENCE
- The Electrochemical Corrosion Behavior of Nanocrystalline 304 Stainless Steel Prepared by Magnetron Sputtering
- (2012) Chen Pan et al. JOURNAL OF THE ELECTROCHEMICAL SOCIETY
- Passive film growth mechanism of nanocrystalline 304 stainless steel prepared by magnetron sputtering and deep rolling techniques
- (2011) Chen Pan et al. ELECTROCHIMICA ACTA
- The influence of crack face contact on the prediction of fatigue crack propagation in residual stress fields
- (2011) D. Schnubel et al. ENGINEERING FRACTURE MECHANICS
- Tensile work hardening behaviour of P91 steel
- (2011) E. Isaac Samuel et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Electrochemical behavior and the rate of general corrosion of NiAl intermetallic compound in the unbuffered sodium chloride solutions
- (2010) K.V. Rybalka et al. CORROSION SCIENCE
- Nucleation of highly dense nanoscale precipitates based on warm laser shock peening
- (2010) Yiliang Liao et al. JOURNAL OF APPLIED PHYSICS
- Strain-induced refinement in a steel with spheroidal cementite subjected to surface mechanical attrition treatment
- (2007) L. Zhou et al. ACTA MATERIALIA
Find the ideal target journal for your manuscript
Explore over 38,000 international journals covering a vast array of academic fields.
SearchCreate your own webinar
Interested in hosting your own webinar? Check the schedule and propose your idea to the Peeref Content Team.
Create Now