Laser-TIG hybrid additive manufacturing; heat treatment; high strength aluminum alloy; microstructure evolution; strengthening mechanism
资金
- National Natural Science Foundation of China [51805070]
After solution + artificial aging treatment (T6 heat treatment) of 2219 aluminum alloy fabricated by laser-tungsten inert gas (TIG) hybrid method, more interestingly, we found that both the strength and elongation were improved. The strengthening mechanism has been analysed in details. Results showed that each layer was divided into the arc zone (AZ) and laser zone (LZ) before and after heat treatment. After T6 heat treatment, the columnar crystal grain morphologies remained the same as the as-deposited condition, while the microstructure presented a strong {001} texture along the building direction. Moreover, the high density of the needle-shaped theta '' phases were uniformly precipitated after artificial aging. Distinct grain morphology, increased the mass fraction of Cu in the Al matrix, and nano-precipitates in the AZ and LZ improved the tensile properties, which exhibited a yield strength of 242.1 +/- 19.6 MPa, an ultimate tensile strength of 407.1 +/- 31.1 MPa, respectively. [GRAPHICS] .
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据