期刊
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T
卷 9, 期 6, 页码 15525-15536出版社
ELSEVIER
DOI: 10.1016/j.jmrt.2020.10.049
关键词
GH909 superalloy; Laser welding; Solidification sequence; Eutectic constituents
资金
- National Natural Science Foundation of China [51705173, 51861165202]
The formation process of gamma/Laves eutectic constituents were systematically investigated in both heat-affected zone (HAZ) and fusion zone (FZ) of laser-welded GH909 superalloy. Solidification sequences and eutectic reactions were proposed by morphologically and chemically analyzing phase and chemical composition by utilizing various characterization methods. In FZ, the ultimate eutectic constituents experienced three stages: 1) liquid (L)-> Primary gamma (gamma) (1360 degrees C), forming a gamma dendritic morphology; 2) following L ->gamma+(Nb, Ti)C precipitation at mushy zone; 3) terminal L ->gamma+Laves (1184 degrees C) at gamma interdendritic regions. Enrichment of Nb in Laves and surrounding gamma produced a high dislocation density in eutectic constituents. Continuous distribution of such gamma/Laves structures promoted the formation of micro interdendritic solidification cracks under accumulated tensile stress. In HAZ, however, the fraction of gamma/Laves constituents was heat input depended and increased as the reduction of distance from fusion line. An interactionally and simultaneously integrated process NbC+gamma -> Laves (similar to 1323 degrees C) caused the formation of eutectic constituents with NbC decomposition, Laves formation, grain boundary liquation and subsequently eutectic reactions. (C) 2020 Published by Elsevier B.V. This is an open access article under the CC BY-NC-ND license
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据