Cell performance enhancement facilitated by mixed ionic and electronic conductor fiber for protonic ceramic fuel cells

This study examines the electrochemical properties of a fibrous composite cathode for protonic ceramic fuel cells (PCFC). Sm0.5Sr0.5CoO3-delta(SSC) fibers having embedded BaCe0.5Zr0.35Y0.15O3-delta(BCZY) particles were fabricated using the electro-spinning process. The BCZY powders were prepared using the conventional citrate-nitrate method. It was subsequently mixed with an SSC solution comprising polyvinylpyrrolidone and aqueous metal nitrate. By electro-spinning the obtained mixture, continuous and longish fibers were obtained, yielding a fiber diameter of 150-200 nm after calcination. The calcined composite nanofibers were deposited via the electrostatic slurry spray deposition technique as a cathode layer on a half-cell comprising NiO and BCZY.According to the results of the single-cell measurement, the fibrous composite cathode exhibited much higher electrochemical properties than a typical nanocomposite cathode over the entire operating temperature range of 550-700 degrees C. Specifically, the polarization resistance of the fibrous composite cathodes was 0.186 omega center dot cm(2)at 700 degrees C, lower than that of a typical nanocomposite cathode. In accordance with the impedance analysis, the maximum power density given by the I-V curve was 642 mW/cm(2)at 700 degrees C, which is regarded as reasonable performance for PCFCs.