COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING
卷 85, 期 -, 页码 31-39出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.compositesa.2016.03.007
关键词
Thermoplastic resin; Interface/interphase; Mechanical testing; Adhesion
Interface thickness and modulus of carbon fiber (CF) reinforced polyamide 6 (PA 6) composites with different thermal histories are characterized as 331-394 nm and 0.24-0.30 times to fiber modulus, respectively. Transverse fiber bundle (TFB) test is firstly employed for evaluating semi-crystalline PA 6 interfacial adhesion. TFB Failure mechanisms are schematically given. Besides enhanced molecular entangling on fiber surface, increased matrix toughness is also found to have a great effect on improved TFB results. Droplet micro-debonding results show that decreasing cooling rate and increasing annealing temperature both decrease interfacial shear strength (IFSS) though residual PA 6 on carbon fiber surface increases. In the end, the above data are normalized together with some previous measured parameters. It shows that quenching of the CF/PA 6 composites and subsequent annealing are shown to give similar results as slow cooling. Relationships between each other are also discussed. (C) 2016 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据