We investigated polydimethylsiloxane/poly(methyl methacrylate) (PDMS/PMMA) interpenetrating polymer networks (IPNs) by both sequential and simultaneous syntheses. In the sequential IPN, the PDMS network was first thermally cured after which methyl methacrylate was swelled in and UV photopolymerized in situ. The simultaneous IPN consists of a one-pot, single-step UV cure of both components. Pure shear fracture and tensile tests were used to extract the Young's modulus, critical fracture strain, and fracture energy of the materials at varying PMMA fractions (up to 50 wt %). At high PMMA fractions, a maximum increase in Young's modulus (42x) and fracture energy (21x) was observed with little sacrifice in the optical properties and the extensibility of notched samples. The Krieger-Dougherty model for particle reinforcement was fit to the modulus data as a function of the PMMA fraction and showed good agreement. The optical properties and microstructure of the IPNs were investigated by UV-visible light transmission, smallangle X-ray scattering (SAXS), and atomic force microscopy (AFM). As the weight fraction of PMMA increased, the simultaneous IPN became less transparent, while the sequential material showed the opposite trend. In the sequential IPN, the minority phase size decreased with increasing PMMA fraction, while it was constant for the simultaneous IPN. Therefore, it was concluded that the sequential IPN transparency is controlled by the size of the PMMA domains, but the simultaneous IPN transparency is controlled by the PMMA fraction. SAXS and AFM also showed evidence of bicontinuous network formation in the simultaneous IPN, which may affect the optical and mechanical properties.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据