The fretting capabilities of 690 alloy against 405 stainless steel were evaluated through a series of tube-plate tests in different experimental conditions. The results indicated that as the temperature increased in air, the wear volume and wear depth increased first until reaching a maximum value at 90 degrees C and then decreased. This was attributed to spinel oxides formed above 200 degrees C in combination with adhesive wear, which contributed to oxidation resistance and a reduction of interfacial wear, resulting in the decrease of wear volume and wear depth. Metallic nickel, iron and chromium were observed in water, which indicated low oxidation, associated with lower wear damage.