INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS
卷 93, 期 -, 页码 -出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ijrmhm.2020.105355
关键词
ZrB2; SiC; Hot-pressing; TEM; Densification; Microstructure
资金
- Natural Sciences and Engineering Research Council of Canada (NSERC) [RGPIN-2016-04221]
- McCain Foundation
This examination is aimed to study the various densification mechanisms in the ZrB2-SiC system at different sintering temperatures. For such an objective, hot-pressing process was implemented to fabricate three ceramics at sintering temperatures of 1650, 1850, and 2050 degrees C under 10 MPa for 1 h. According to the results, particle rearrangement and fragmentation were the predominant densification mechanisms at the lowest sintering temperature. Additionally, it was found that the activation of the liquid phase sintering mechanism was advantageous in the particle rearrangement at low temperatures. However, rising the sintering temperature to 1850 degrees C changed the dominant mechanism to the plastic deformation. Such a phenomenon was accompanied by the creation of many dislocations in both ZrB2 and SiC grains. Implementing a higher sintering temperature (2050 degrees C) activated another consolidation mechanism called diffusion. This occurrence, together with the evaporation of the majority of the liquid phase at elevated temperatures, resulted in emerging transgranular fracture mode in the sample.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据