标题
Hydrogen Permeation in X65 Steel under Cyclic Loading
作者
关键词
-
出版物
Materials
Volume 13, Issue 10, Pages 2309
出版商
MDPI AG
发表日期
2020-05-18
DOI
10.3390/ma13102309
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- Investigation of Hydrogen Embrittlement Susceptibility and Fracture Toughness Drop after in situ Hydrogen Cathodic Charging for an X65 Pipeline Steel
- (2020) Helen Kyriakopoulou et al. Micromachines
- Quantification of Temperature Dependence of Hydrogen Embrittlement in Pipeline Steel
- (2019) Xiao Xing et al. Materials
- Hydrogen diffusion in low alloy steels under cyclic loading
- (2019) Marina Cabrini et al. CORROSION REVIEWS
- The synergistic action and interplay of hydrogen embrittlement mechanisms in steels and iron: Localized plasticity and decohesion
- (2019) Milos B. Djukic et al. ENGINEERING FRACTURE MECHANICS
- Hydrogen induced blister cracking and mechanical failure in X65 pipeline steels
- (2019) Vishal Singh et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- Hydrogen Embrittlement Evaluation of Micro Alloyed Steels by Means of J-Integral Curve
- (2019) Marina Cabrini et al. Materials
- Effects of alloying elements on vacancies and vacancy-hydrogen clusters at coherent twin boundaries in nickel alloys
- (2018) Xiao Zhou et al. ACTA MATERIALIA
- Comparison of hydrogen embrittlement susceptibility of three cathodic protected subsea pipeline steels from a point of view of hydrogen permeation
- (2018) Timing Zhang et al. CORROSION SCIENCE
- An extended engineering critical assessment for corrosion fatigue of subsea pipeline steels
- (2018) Ankang Cheng et al. ENGINEERING FAILURE ANALYSIS
- Reduction of hydrogen embrittlement of API 5l X65 steel pipe using a green inhibitor
- (2018) M. Soudani et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- Hydrogen related degradation in pipeline steel: A review
- (2018) Enyinnaya Ohaeri et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- Corrosion Crack Nucleation Mechanism in the Welded Structures of X65 Steel in Natural Seawater
- (2018) Linyue Bai et al. Advances in Materials Science and Engineering
- Effect of Temperature on Corrosion and Cathodic Protection of X65 Pipeline Steel in 3.5% NaCl Solution
- (2018) Yingjie Liu et al. International Journal of Electrochemical Science
- Corrosion behavior of hydrogen charged super duplex stainless steel welded joints
- (2017) A. Świerczyńska et al. MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION
- The mutual effects of hydrogen and microstructure on hardness and impact energy of SMA welds in X65 steel
- (2017) Amin Latifi V. et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Cathodic protection modelling of a propeller shaft
- (2016) Sergio Lorenzi et al. CORROSION SCIENCE
- The effect of TiC on the hydrogen induced ductility loss and trapping behavior of Fe-C-Ti alloys
- (2016) T. Depover et al. CORROSION SCIENCE
- Effects of microstructure banding on hydrogen assisted fatigue crack growth in X65 pipeline steels
- (2016) Joseph A. Ronevich et al. INTERNATIONAL JOURNAL OF FATIGUE
- The effect of hydrogen on stress corrosion behavior of X65 steel welded joint in simulated deep sea environment
- (2016) Hongxia Wan et al. OCEAN ENGINEERING
- Multiscale description of dislocation induced nano-hydrides
- (2015) G.P.M. Leyson et al. ACTA MATERIALIA
- Environmentally assisted cracking and hydrogen diffusion in traditional and high-strength pipeline steels
- (2015) Marina Cabrini et al. CORROSION REVIEWS
- Mechanisms of hydrogen-enhanced localized plasticity: An atomistic study using α-Fe as a model system
- (2014) J. Song et al. ACTA MATERIALIA
- Hydrogen diffusion into three metallurgical microstructures of a C–Mn X65 and low alloy F22 sour service steel pipelines
- (2014) E. Fallahmohammadi et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- Hydrogen Embrittlement of Ferritic Steels: Deformation and Failure Mechanisms and Challenges in the Oil and Gas Industry
- (2014) R. Srinivasan et al. JOM
- Effects of Prior Cold Work on Hydrogen Trapping and Diffusion in API X-70 Line Pipe Steel During Electrochemical Charging
- (2013) Hung M. Ha et al. CORROSION
- A fracture criterion for the notch strength of high strength steels in the presence of hydrogen
- (2013) C. Ayas et al. JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS
- Atomic mechanism and prediction of hydrogen embrittlement in iron
- (2012) Jun Song et al. NATURE MATERIALS
- Hydrogen embrittlement behavior of HSLA line pipe steel under cathodic protection
- (2011) Marina Cabrini et al. CORROSION REVIEWS
- Hydrogen interaction with multiple traps: Can it be used to mitigate embrittlement?
- (2011) M. Dadfarnia et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- First-principles study on the interaction of H interstitials with grain boundaries inα- andγ-Fe
- (2011) Yaojun A. Du et al. PHYSICAL REVIEW B
- A nanoscale mechanism of hydrogen embrittlement in metals
- (2010) Jun Song et al. ACTA MATERIALIA
- Effect of microstructure on the hydrogen trapping efficiency and hydrogen induced cracking of linepipe steel
- (2008) Gyu Tae Park et al. CORROSION SCIENCE
Find the ideal target journal for your manuscript
Explore over 38,000 international journals covering a vast array of academic fields.
SearchCreate your own webinar
Interested in hosting your own webinar? Check the schedule and propose your idea to the Peeref Content Team.
Create Now