Laser welding; Hybrid welding; High strength steel; Thick steel; Mechanical properties; Toughness
资金
- SINTEF AS
- Statens vegvesen AS (Norway)
High-power lasers are very effective in welding of plates thicker than 10 mm due to the keyhole mode. High-power intensity generates a vapor-filled cavity which provides substantial penetration depth. Due to the narrow and deep weld geometry, there is susceptibility to high hardness and weld defects. Imperfections occur due to keyhole instability. A 16-kW disk laser was used for single-pass welding of 12- to 15-mm thick plates in a butt joint configuration. Root humping was the main imperfection and persisted within a wide range of process parameters. Added arc source to the laser beam process may cause increased root humping and sagging due to accelerated melt flow. Humping was mitigated by balancing certain arc and other process parameters. It was also found that lower welding speeds (< 1.2 m/min) combined with lower laser beam power (< 13 kW) can be more positive for suppression of humping. Machined edges provided more consistent root quality and integrity compared with plasma cut welded specimens. Higher heat input (> 0.80 kJ/mm) welds provided hardness level below 325 HV. The welded joints had good Charpy toughness at - 50 degrees C (> 50 J) and high tensile strength.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据