卷 42, 期 9, 页码 11077-11084出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2016.04.006
关键词
High-energy ball milling; Nanostructured composites; Nitrides; Spark plasma sintering
The present study focused on the fabrication of bulk materials from Ti1-xAlxN nano-powders using a spark plasma sintering (SPS) apparatus. Super-saturated Ti1-xAlxN solid solutions containing differing fractions of AlN (10, 20, 30 and 50 mol%) were synthesized by high-energy ball milling (HEBM) of pure nitrides. The complete dissolution of AlN in TiN was achieved after 100 h of milling. The milled powders were characterized by X-ray diffraction, scanning electron microscopy, energy-filtered transmission electron microscopy spectra imaging and energy dispersive X-ray spectroscopy. The crystalline size of the mechanically alloyed powders after 100 h of milling was about 12-14 nm. Ti1-xAlxN powders of various compositions were sintered by SPS under pressure of 63 MPa at 1673 K. Maximal hardness and bending strength values (610 MPa and 18.6 GPa, respectively) were obtained for composites containing 20 mol% AlN. Powder with 20% mole%AlN was consolidated under pressure of 500 MPa in the 1273-1423K temperature range by high pressure SPS (HPSPS). A fully dense nano-structured specimen, processed at 1423 K, displayed a Young modulus of 420 GPa, hardness of 20.5 GPa, bending strength of 670 MPa and fracture toughness of 7.1 MPa m(0.5). (C) 2016 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据