Thermoelectric material; Anti-oxidation; Plasma spray; Mg2Si
资金
- National Research Foundation of Korea - Korean Government (MSIP) [NRF-2015R1A5A1036133]
Oxide-based coating layers were investigated to suppress the oxidation of an intermediate temperature thermoelectric module that operates in a temperature range of 300-700 degrees C. Four different oxides [alumina (Al2O3), yttria (Y2O3), 8 mol% yttria-stabilized zirconia ((Y2O3)(0.08)(ZrO2)(0.92), YSZ), and 20 mol% samaria-doped ceria (Sm0.2Ce0.8O1.9, SDC)] were coated onto Mg2Si thermoelectric leg surfaces and their anti-oxidation characteristics were compared. While Al2O3, Y2O3, and SDC layers failed to prevent the progression of oxidation of the thermoelectric Mg2Si surface at 700 degrees C, YSZ showed potential as an anti oxidation coating layer for intermediate temperature thermoelectric modules. The apparent oxidation suppression characteristics of the YSZ layer on the Mg2Si thermoelectric material were studied by a microstructural investigation of the interface between the coated layer and the thermoelectric material. The reliability of the YSZ coating structure was investigated via thermal cycling tests from room temperature to 600 The practical adaptability of the YSZ anti-oxidation coating in terms of use for thermoelectric power-generation modules is discussed in detail with the results of variation in contact resistance. (C) 2016 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据