期刊
CEMENT AND CONCRETE RESEARCH
卷 85, 期 -, 页码 183-191出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.cemconres.2015.12.016
关键词
Thermal treatment; Microstructure; Physical properties; Cement manufacture; Carbon utilisation in nesquehonite
资金
- Gulf Organization of Research and Development (GORD) in Qatar [RG11757-10]
Magnesium from reject desalination brine is reacted at atmospheric pressure and 25-65 degrees C with CO2 from industrial effluent combustion gas, precipitating preferably nesquehonite, MgCO3 center dot 3H(2)O. Nesquehonite can be thermally activated so that, when remixed with water, it is self-cementing. At ambient temperature, cure durations are typically similar to 1-3 days. The nesquehonite-based product contains similar to 32 wt sequestered carbon dioxide and, at end of use, can be recycled without loss of CO2. As an application example, cast nesquehonite products are suitable to form lightweight, incombustible building materials with densities in the range 700-900 kg/m(3). Compressive strengths of the cast products are low, ca 2-4 MPa, thus application is envisaged to be broadly similar to that of gypsum-based products. (C) 2016 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据