MICROMACHINES
卷 11, 期 2, 页码 -出版社
MDPI
DOI: 10.3390/mi11020180
关键词
Co thin films; XRD; pop-in; nanoindentation
类别
资金
- Ministry of Science and Technology, Taiwan [MOST107-2112-M-214-001]
The correlations between the microstructure and nanomechanical properties of a series of thermal annealed Co thin films were investigated. The Co thin films were deposited on glass substrates using a magnetron sputtering system at ambient conditions followed by subsequent annealing conducted at various temperatures ranging from 300 degrees C to 800 degrees C. The XRD results indicated that for annealing temperature in the ranged from 300 degrees C to 500 degrees C, the Co thin films were of single hexagonal close-packed (hcp) phase. Nevertheless, the coexistence of hcp-Co (002) and face-centered cubic (fcc-Co (111)) phases was evidently observed for films annealed at 600 degrees C. Further increasing the annealing temperature to 700 degrees C and 800 degrees C, the films evidently turned into fcc-Co (111). Moreover, significant variations in the hardness and Young's modulus are observed by continuous stiffness nanoindentation measurement for films annealed at different temperatures. The correlations between structures and properties are discussed.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据