Titanium alloy; High temperature; Powder metallurgy; Tensile properties; Silicide
类别
资金
- National Natural Science Funds for Distinguished Young Scholar of China [51625404]
The service temperature of high temperature titanium alloy has been raised from 400 degrees C to 650 degrees C in the last years. In this study, a new near a high temperature titanium alloy with high Si content (Ti-6Al-4Zr-0.5Mo-0.6Si, wt. %) which can serve at 700 degrees C was developed by powder metallurgy (P/M) method. The microstructure and mechanical properties were investigated. The results show that the P/M titanium alloy exhibits an alpha + beta two-phase microstructure with dispersed fine S-2 type silicide ((TiZr)(6)Si-3). The yield strength and ultimate tensile strength are 1023 MPa and 1190 MPa at room temperature, with an elongation of 10%. At 700 degrees C, the alloy still maintains a yield strength, an ultimate strength, and an elongation of 510 MPa, 651 MPa and 13%, respectively. The high strength is mainly attributed to the precipitation strengthening of the silicide and the formation of flne-grained alpha' phase.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据