Polydopamine exhibits high potential as coating of materials used for medical devices, antifouling, and corrosion prevention. Repetitive cyclic voltammetry on gold electrodes was used to deposit polydopamine by anodic oxidation. Investigation of polydopamine formation in the pH range 5-8 showed that coating at pH 6.5 permits selective polydopamine formation on the electrode, while auto-oxidation of dopamine in the electrolyte could be suppressed. The optimized conditions then were transferred to stainless steel electrodes. At pH 6.5-6.6, an anodic peak current density of 12.9 mu A/mm( )(2)was measured using a plane stainless steel anode in 5 mM dopamine solution. During experimental scale-up, anodic coating of 1.4622 steel plates in galvanostatic experiments led to formation of a colored polydopamine surface, which exhibited reduction of the water contact angle by 13.5 degrees. The controlled anodic polydopamine formation is of a particular value for an economic polydopamine coating of the conductive material in larger-scale applications.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据