Omniphobic re-entrant PVDF membrane with ZnO nanoparticles composite for desalination of low surface tension oily seawater

In this study, an omniphobic membrane was fabricated by electrospraying fluorinated zinc oxide (ZnO) nanoparticles (NPs) mixed with polyvinylidene fluoride-co-hexafluoropropylene (PVDF-HFP) on the surface of an organosilane functionalized polyvinylidene difluoride (PVDF) membrane. Our results revealed that the functionalized ZnO NPs membrane exhibited a rough hierarchical re-entrant morphology with low surface energy which allowed it to achieve high omniphobic characteristics. It was observed that the addition of 30% ZnO (w/w of PVDF-HFP) was found to be optimal and imparted a high repulsive characteristic. The optimized PVDF/ZnO(30)/FAS/PVDF-HFP referred as cPFP-30Z membrane exhibited a high contact angle values of 159.0 +/- 3.1 degrees, 129.6 +/- 2.2 degrees, 130.4 +/- 4.1 degrees and 126.1 +/- 1.2 degrees for water, sodium dodecyl sulfate (SDS) saline solution (0.3 mM SDS in 3.5% NaCl), ethanol, and vegetable oil, respectively. The low surface energy and high surface roughness (Ra) of optimised membrane was assessed as 0.78 +/- 0.14 mN m(-1) and 1.37 mu m, respectively. Additionally, in contrast with the commercial PVDF membrane, the cPFP-30Z membrane exhibited superior anti-wetting/anti-fouling characteristics and high salt rejection performance (>99%) when operated with a saline oil solution (0.015 v/v) and SDS (0.4 mM) feed solutions. (C) 2019 Elsevier Ltd. All rights reserved.